Abstract:Biodegradable metals (BM) and additive manufacturing (AM) are regarded revolutionary biomaterials and biofabrication technologies for bone repairing metal implants, the combination of both, namely AM of BM, is thus expected to solve the dual technical difficulties including "conventional medical metals are biologically inert and exist in the human body permanently" and "conventional manufacturing processes are inadequate to fabricate personalized implants of complicated structure". This work additively manufactured biodegradable Zn-Mg alloy porous scaffolds by laser powder bed fusion (L-PBF). By using the pre-alloyed Zn-xMg (x = 1, 2 and 5 wt.%) powder and the optimized processing conditions, high fusion quality with the relative density greater than 99.5% was confirmed for the L-PBF parts. The influence of Mg content on microstructure, mechanical properties, in vitro corrosion, cytocompatibility, in vivo degradation, biocompatibility and osteogenic effect was investigated. Fine α-Zn grains and precipitation phases including Mg2Zn11 and MgZn2 were observed in the Zn-xMg L-PBF parts. The hardness increased, and the strength increases firstly and then decreased with increasing the Mg content. The compressive strength and elastic modulus of Zn-1Mg porous scaffolds reached the highest as 40.9 ± 0.4 MPa and 1.17 ± 0.11 GPa respectively, equivalent to those of cancellous bone. The corrosion rate and cell viability slightly rose with increasing the Mg content. Histological analysis after 6-week and 12-week implantation in rabbit femurs showed enhanced bone formation around the Zn-1Mg porous scaffolds compared with pure Zn counterparts. In summary, Zn-1Mg porous scaffolds produced by L-PBF presented promising results to fulfill customized requirements of biodegradable bone implants.Statement of significanceAdditive manufacturing of biodegradable metal porous scaffolds is expected to solve the dual challenges from customized structures and bioactive function required for bone implants. It was the first to present a systematic in vitro and in vivo investigation into the compositions, microstructure, mechanical properties, biodegradation, biocompatibility and osteogenic effect of additively manufactured Zn-Mg alloy porous scaffolds. Reliable formation quality and performance evaluation was achieved by using the pre-alloyed Zn-xMg (x=1, 2 and 5 wt.%) powder and the optimized laser powder bed fusion process. Although the Zn-1Mg scaffolds exhibited promising mechanical strength, biocompatibility, and osteogenic effect, their degradation rate needs to be further accelerated compared with the term of bone reconstruction.

Compression properties, in vitro degradation behavior and biocompatibility of porous Mg-1Zn-1Ca-0.5Mn alloy scaffolds with different pore parameters

Microstructure, Mechanical Properties, and Corrosion Resistance of Porous Bio Mg Alloy Scaffolds Prepared via a Novel Method

Porous Mg–Zn–Ca scaffolds for bone repair: a study on microstructure, mechanical properties and in vitro degradation behavior

Mechanical Properties, Biodegradation, and Biocompatibility of Porous Mg Alloy Scaffolds for Load Bearing Bone Applications

Effect of pore geometry on properties of high-temperature oxidized additively manufactured magnesium scaffolds

Synthesis, microstructure and mechanical properties of porous Mg--Zn scaffolds

Research on corrosion behavior and biocompatibility of a porous Mg-3%Zn/5%β-Ca3(PO4)2 composite scaffold for bone tissue engineering

Mechanical properties, in vitro biodegradable behavior, biocompatibility and osteogenic ability of additively manufactured Zn-0.8Li-0.1Mg alloy scaffolds

Preparation and in Vitro Degradation Behavior of Biodegradable Porous Zn-Li-Ca Alloy Bone Repair Scaffolds

Exploration of microstructural characteristics, mechanical properties, and in vitro biocompatibility of biodegradable porous magnesium scaffolds for orthopaedic implants

Extrusion-based additive manufacturing of Mg-Zn alloy scaffolds

MgF2-coated porous magnesium/alumina scaffolds with improved strength, corrosion resistance, and biological performance for biomedical applications

3D Printing of a Porous Zn-1Mg-0.1Sr Alloy Scaffold: A Study on Mechanical Properties, Degradability, and Biosafety

The effect of pore size on the mechanical properties, biodegradation and osteogenic effects of additively manufactured magnesium scaffolds after high temperature oxidation: An in vitro and in vivo study

In Vitro and in Vivo Studies on As-Extruded Mg- 5.25Wt.%zn-0.6Wt.%ca Alloy As Biodegradable Metal

3D-cubic interconnected porous Mg-based scaffolds for bone repair

Additive manufacturing of Zn-Mg alloy porous scaffolds with enhanced osseointegration: In vitro and in vivo studies

Effects of MgO Nanoparticle Addition on the Mechanical Properties, Degradation Properties, Antibacterial Properties and in Vitro and in Vivo Biological Properties of 3D-Printed Zn Scaffolds

Evaluation on the corrosion resistance, antibacterial property and osteogenic activity of biodegradable Mg-Ca and Mg-Ca-Zn-Ag alloys

Development of biodegradable Zn-based porous scaffolds with elaborate triply periodic minimal surface structure via Vat photopolymerization-assisted template replacement strategy

Microstructure, Mechanical Properties, Corrosion Behavior and Biocompatibility of As-Extruded Biodegradable Mg–3Sn–1Zn–0.5Mn Alloy