Abstract:Magnesium shows promising properties concerning its use in absorbable implant applications such as biodegradability, improved mechanical strength and plastic deformability. Following extensive research, the first fixation and compression screws composed of magnesium rare earth alloys were commercialised, notably in the field of orthopaedic surgery. Preclinical and clinical follow-up studies showed that the rapid degradation of unprotected metallic Magnesium surfaces and concomitant hydrogen gas bursts still raise concern regarding certain surgical indications and need to be further improved. In order to enlarge the scope of further applications, the development of future magnesium implants must aim at freedom of design and reduction of volume, hereby enabling higher functionalised implants, as e.g. plate systems or scaffold grafts for bone replacement therapy. In order to overcome the boundaries of conventional manufacturing methods such as turning or milling, the process of Laser Powder Bed Fusion (LPBF) for magnesium alloys was recently introduced. It enables the production of lattice structures, therefore allowing for reduction of implant material volume. Nevertheless, the concomitant increase of free surface of such magnesium scaffolds further stresses the aforementioned disadvantages of vast degradation and early loss of mechanical stability if not prevented by suitable postprocessing methods. Magnesium scaffold structures with different pore sizes were therefore manufactured by LPBF and consequently further modified either by thermal heat treatment or Plasma Electrolytic Oxidation (PEO). Implant performance was assessed by conducting degradation studies and mechanical testing. PEO modified scaffolds with small pore sizes exhibited improved long-term stability, while heat treated specimens showed impaired performance regarding degradation and mechanical stability. STATEMENT OF SIGNIFICANCE: Magnesium based scaffold structures offer wide possibilities for advanced functionalized bioabsorbable implants. By implementing lattice structures, big implant sizes and mechanically optimized implant geometries can be achieved enabling full bone replacement or large-scale plate systems, e.g. for orthopedic applications. As shape optimization and lattice structuring of such scaffolds consequently lead to enlarged surface, suitable design and postprocessing routines come into focus. The presented study addresses these new and relevant topics for the first time by evaluating geometry as well as heat and surface treatment options as input parameters for improved chemical and mechanical stability. The outcome of these variations is measured by degradation tests and mechanical analysis. Evaluating these methods, a significant contribution to the development of absorbable magnesium scaffolds is made. The findings can help to better understand the interdependence of high surface to volume ratio Magnesium implants and to deliver methods to incorporate such lattice structures into future large-scale implant applications manufactured from bioabsorbable Magnesium alloys.

The effect of pore size on the mechanical properties, biodegradation and osteogenic effects of additively manufactured magnesium scaffolds after high temperature oxidation: An in vitro and in vivo study

Effect of pore geometry on properties of high-temperature oxidized additively manufactured magnesium scaffolds

The Biological Properties of 3D-Printed Degradable Magnesium Alloy WE43 Porous Scaffolds Via the Oxidative Heat Strategy

Effect of pore size on tissue ingrowth and osteoconductivity in biodegradable Mg alloy scaffolds

Compression properties, in vitro degradation behavior and biocompatibility of porous Mg-1Zn-1Ca-0.5Mn alloy scaffolds with different pore parameters

Additive manufacturing of porous magnesium alloys for biodegradable orthopedic implants: process, design, and modification

A novel open-porous magnesium scaffold with controllable microstructures and properties for bone regeneration

An Animal Experimental Study of Porous Magnesium Scaffold Degradation and Osteogenesis

Biodegradable magnesium alloy WE43 porous scaffolds fabricated by laser powder bed fusion for orthopedic applications: Process optimization, in vitro and in vivo investigation

The in Vitro and in Vivo Biological Effects and Osteogenic Activity of Novel Biodegradable Porous Mg Alloy Scaffolds

3D Printing Magnesium-Doped Wollastonite/β-Tcp Bioceramics Scaffolds with High Strength and Adjustable Degradation

Microstructure, Mechanical Properties, and Corrosion Resistance of Porous Bio Mg Alloy Scaffolds Prepared via a Novel Method

Magnesium surface-activated 3D printed porous PEEK scaffolds for in vivo osseointegration by promoting angiogenesis and osteogenesis

Multi-scale mechanical and morphological characterisation of sintered porous magnesium-based scaffolds for bone regeneration in critical-sized defects

Biofunctional magnesium coated Ti6Al4V scaffold enhances osteogenesis and angiogenesis in vitro and in vivo for orthopedic application

Porous Mg–Zn–Ca scaffolds for bone repair: a study on microstructure, mechanical properties and in vitro degradation behavior

A biodegradable 3D woven magnesium-based scaffold for orthopedic implants

Preparation, Mechanical Properties and in Vitro Biodegradation of Porous Magnesium Scaffolds

Influence of design and postprocessing parameters on the degradation behavior and mechanical properties of additively manufactured magnesium scaffolds

Effects of MgO Nanoparticle Addition on the Mechanical Properties, Degradation Properties, Antibacterial Properties and in Vitro and in Vivo Biological Properties of 3D-Printed Zn Scaffolds

MgF2-coated porous magnesium/alumina scaffolds with improved strength, corrosion resistance, and biological performance for biomedical applications