Evaluation of Li 2 SnO 3 :Cr 3+ , Mn 4+ as a dual-emitter luminescence sensor for cryogenic temperatures

V. Mykhaylyk,Y. Zhydachevskyy,H. Kraus,V. Stasiv,G. Leniec,V. Hreb,L. Vasylechko,V. Sydorchuk,A. Suchocki

DOI: https://doi.org/10.1039/d3tc03913g

IF: 6.4

2024-01-01

Journal of Materials Chemistry C

Abstract:The sensitivity of luminescence properties in materials doped with transition metal (TM) ions to changes of temperature makes them particularly promising for thermometric applications.

materials science, multidisciplinary,physics, applied

What problem does this paper attempt to address?

This paper aims to explore the potential of Li_2SnO_3:Cr^3+,Mn^4+ as a dual - emission fluorescent material for low - temperature temperature sensors. Specifically, the research focuses on the following aspects:

1. **Material Selection and Characteristics**: Li_2SnO_3 was selected as the host material because it can accommodate Cr^3+ and Mn^4+ ions simultaneously at the Sn octahedral sites. Cr^3+ and Mn^4+ ions exhibit different luminescence characteristics in crystal fields of different intensities. Among them, Mn^4+ ions show obvious 2E - 4A2 line emission due to the strong crystal - field effect, while Cr^3+ ions show both 2E - 4A2 and 4T2 - 4A2 emissions due to the medium - strength crystal - field effect.

2. **Structural Analysis**: Through powder X - ray diffraction (XRD), electron paramagnetic resonance (EPR) and photoluminescence techniques, the researchers identified two different types of [SnO_6] octahedral centers, which correspond to two slightly different Cr^3+ and Mn^4+ emission centers in the Li_2SnO_3 structure.

3. **Temperature Sensitivity**: It was found that the decay time constant of the 2E - 4A2 emission of Li_2SnO_3:Cr^3+,Mn^4+ is very sensitive to temperature changes (2.0%/K at 190 K and 5.8%/K at 220 K), which makes this material a potential candidate for non - contact temperature sensors.

4. **Advantages of Dual - Emission Materials**: Using this dual - emission fluorescent material as a temperature sensor can expand its sensitive range and provide the advantage of cross - validation measurement, and has a broader application prospect compared with materials doped with only Cr^3+ or Mn^4+.

### Formula Summary

- **EPR Spectral Line Position Formula**:
\[
g_{\text{eff}}=\frac{7144.773 f_{\text{res}}(\text{GHz})}{B_{\text{res}}(\text{mT})}
\]
where \( f_{\text{res}} \) is the microwave frequency and \( B_{\text{res}} \) is the position of the resonance line in the magnetic field.

- **Spin Hamiltonian Parameters**:
\[
H_{\text{Cr}^{3+}/C_0/C_1}=H_{\text{Zeeman}}+H_{\text{ZFS}}
\]
\[
H_{\text{Mn}^{4+}/C_0/C_1}=H_{\text{Zeeman}}+H_{\text{ZFS}}+H_{\text{HF}}
\]
\[
H_{\text{Zeeman}}=\mu_B B g S
\]
\[
H_{\text{ZFS}}=D S_z^2+\frac{1}{3}(S\cdot S + 1)-\frac{E}{8}(S_x^2+S_y^2)
\]
\[
H_{\text{HF}}=S\cdot A\cdot I
\]
where \( \mu_B \) is the Bohr magneton, \( B \) is the magnetic field induction, \( g \) is the spectroscopic splitting factor, \( S \) is the electron spin, \( D \) and \( E \) are the axial and rhombic distortions respectively, \( A \) is the hyperfine interaction matrix, and \( I \) is the nuclear spin.

- **Temperature - Dependent Fitting Formula**:
\[
I(T)=\frac{I_0}{1 + C_1\exp\left(-\frac{E_1}{kT}\right)+C_2\exp\left(-\frac{E_2}{kT}\right)}
\]
\[
I(T)=\frac{I_0\left(1 + A_1\exp\left(-\frac{E_0_1}{kT}\right)\right)}{1 + C_1\exp