Abstract:Modern Physics Letters B, Ahead of Print. Annealing at high temperatures holds the possibility of concentrating defects in the graphene. Moreover, a significant increase in annealing temperature destroys the surface properties. In this work, the reduced graphene oxide (RGO) was prepared by an electrochemical technique with a high voltage ([math][math]V, [math][math]A). Then, the potential effects of impact on thermal treatment in a temperature range of 800–1000∘C in nitrogen-rich environment on the microstructure and surface morphology, thermal stability, phase and crystallinity, structural disorder, absorption properties, and optical properties of RGO for optoelectronic applications were investigated. In addition, a link was established between the estimated crystallite sizes determined by X-ray diffraction (XRD) and Raman data. The microstructural data indicate that the annealing temperature has a significant effect on the microstructure and carbon–oxygen (C/O) ratio. The C/O ratio increases as a function of annealing temperature. Atomic force microscope (AFM) analysis revealed that the root mean square (RMS) roughness of annealed RGO increases with increasing annealing temperature indicating an increase in crystallite size during annealing. Since most organic compounds were removed from the surface of the annealed RGO, oxygen functionalities appear to have minimal effect on the thermal stability of RGO. The size of graphene crystallites increases with annealing temperature, as shown by XRD observations. The crystalline structure was restored by annealing. The Raman results show that in the "low" defect density zone, the [math] values increase because a larger defect density causes a stronger elastic scattering. UV–Vis spectroscopy shows that the absorption of RGO is not affected by annealing temperatures between 800∘C and 900∘C. The optical bandgap of annealed RGOs decreases from 4.08 to 3.72[math]eV upon annealing in the temperature range of 800–1000∘C.

Tracking interfacial changes of graphene/Ge(110) during in-vacuum annealing

Surface Reconstruction of Germanium: Hydrogen Intercalation and Graphene Protection

Effects of Defects and Thermal Treatment on the Properties of Graphene

Probing post-growth hydrogen intercalation and H 2 nanobubbles formation in graphene on Ge(110)

Thermal annealing of exfoliated graphene

Gas Sensing Performance of Graphene-Metal Contact after Thermal Annealing

Defects in GaN Films Studied by Positron Annihilation Spectroscopy

The annealing effect of chemical vapor deposited graphene

Graphene Annealing: How Clean Can It Be?

Influence of Annealing on Raman Spectrum of Graphene in Different Gaseous Environments

Effect of substrate polishing on the growth of graphene on 3C–SiC(111)/Si(111) by high temperature annealing

Evaluation of graphene microstructural and optical properties affected by high-temperature annealing and rapid cooling in a nitrogen-rich environment

Toward intrinsic graphene surfaces: a systematic study on thermal annealing and wet-chemical treatment of SiO2-supported graphene devices

Effects of Annealing Parameters on Epitaxial Graphene on SiC Substrates

Periodic ripples on thermally annealed Graphene on Cu (110) - Surface reconstruction or Moire pattern?

Effect of Hydrogen Annealing on the Property of Low-temperature Epitaxial Growth of Sige Thin Films on Si Substrate

Thermally Induced Surface Faceting on Heteroepitaxial Layers

Raman analysis of the dehydrogenation process of hydrogenated monolayer graphene

Driving with temperature the synthesis of graphene films on Ge(110)

Annealing Time Dependence of Morphology and Structure of Epitaxial Graphene on 6H-SiC(0001) Surface

Quantitative Analysis of Structure and Bandgap Changes in Graphene Oxide Nanoribbons During Thermal Annealing