Study on the fretting maps of Zircaloy-4 alloy against Inconel 718 alloy

Xinlu Yuan,Xiaoyu Zhang,Qiang Zhang,Jian Pu,Li,Pingdi Ren,Minhao Zhu,Gen Li

DOI: https://doi.org/10.1016/j.triboint.2021.107024

IF: 5.62

2021-08-01

Tribology International

Abstract:Fretting wear tests of Zircaloy-4 alloy against Inconel 718 alloy were conducted on a fretting wear rig. The contact state and fretting running characteristics of Zircaloy-4 alloy were investigated. The running condition fretting map of Zircaloy-4 alloy presents three regimes, namely, partial slip regime, mixed slip regime, and gross slip regime. Slight degradation was observed in the partial slip regime. In the mixed slip regime, adhesive wear of the stick zone and oxidation wear of the slip zone are the main damage mechanisms, and cracking was observed at the stick-slip boundary. Severe material detachment due to wear is predominant in the gross slip regime, and the main damage mechanisms are adhesion, plastic deformation, surface fatigue, frictional oxidation and abrasion.

engineering, mechanical

What problem does this paper attempt to address?

The paper primarily investigates the friction and wear characteristics between Zircaloy-4 alloy and Inconel 718 alloy, and attempts to establish fretting maps between these two materials. The core issue of the study is to understand the friction behavior and related damage mechanisms under different contact conditions, with the aim of reducing premature failure of critical components in nuclear reactor systems due to friction.

Specifically, the study attempts to address the following aspects:

1. **Construction of Fretting Maps**: By experimentally testing the friction and wear characteristics of Zircaloy-4 alloy and Inconel 718 alloy under different contact conditions, the study aims to construct fretting maps between the two materials. These fretting maps can help engineers identify surface degradation characteristics and damage mechanisms of different materials under specific conditions.

2. **Contact State Analysis**: The study analyzes the contact states under different contact conditions (such as contact force, friction displacement, etc.), including partial slip, mixed slip, and gross slip states. These different contact states have a significant impact on the wear of the materials.

3. **Investigation of Damage Mechanisms**: The study explores the main damage mechanisms on the material surface under the aforementioned different contact states. For example, in the partial slip state, slight adhesive wear and oxidative wear are the main forms of damage; whereas in the gross slip state, severe material detachment may occur, and the damage mechanisms mainly include adhesion, plastic deformation, surface fatigue, friction oxidation, and abrasive wear.

In summary, this study aims to deeply understand the friction and wear characteristics and damage mechanisms of Zircaloy-4 alloy and Inconel 718 alloy under different contact conditions through experimental means, providing theoretical basis and technical support for mitigating damage to critical components in nuclear reactor systems caused by friction.