Effect of La and Cu Co-Doping on Structural Evolution and High-Frequency Magnetic and Dielectric Properties of Z-type Hexaferrites
Yida Lei,Kui Liu,Xingyu Huo,Yang Xiao,Yanlin Ma,Shifan Lu,Huaiwu Zhang,Jie Li
DOI: https://doi.org/10.1016/j.ceramint.2024.11.398
IF: 5.532
2024-01-01
Ceramics International
Abstract:A series of La and Cu co-doped high-density Z-type hexaferrites, namely Ba3−xLaxCo2Fe24−xCuxO41 (x = 0.20–0.95 in steps of 0.15), were synthesized via solid-state reaction method. Phase composition, microstructure, static magnetic properties, and high-frequency magneto–dielectric properties were studied systematically. Results show that with the addition of La and Cu, initial Z-type phase gradually transforms into a combination of Z- and W-type phases, and grain size increases. Specific saturation magnetization of samples increases significantly with increasing x and reaches the maximum (σs = 59.20 emu/g) at x = 0.95. Furthermore, high-frequency magnetic and dielectric properties are improved, with permeability μ' and permittivity ε′ becoming almost equal in 0.1–1 GHz band. In particular, the sample with x = 0.65 exhibits excellent Snoek's product, that is , normalized impedance approaches 1, and miniaturization factor is around 13.45 (@500 MHz). In this case, dielectric loss tangent tan δε is less than 0.003 below 500 MHz, and frequency range in which magnetic quality factor Q is greater than 10 is significantly broadened, covering wide bandwidth from 10 to 580 MHz. Thus, these hexaferrite ceramics are significantly promising for application to microwave communications.