THE METAL-INSULATOR TRANSITION IN Na0.75Co1-xRuxO2
HANG-DONG WANG,JIN-HU YANG,QI LI,HAI-YANG WANG,MING-HU FANG,Wei Zhang,kazuyoshi Yoshimura
DOI: https://doi.org/10.3969/j.issn.1000-3258.2005.z1.009
2005-01-01
Abstract:The measurements of structure, resistivity, and magnetic properties were carried out for Na_ 0.75 Co_ 1-x Ru_ x O_ 2 (0x0.5)samples, which were prepared by a solid state reaction method. It is found that the unit cell parameter a and c values increase monotonously with the increasing Ru partial concentration, which indicates that the partial substitution of Ru for Co in Na_ 0.75 Co_ 1-x Ru_ x O_ 2 system is uniform and the structure of Na_ 0.75 Co_ 1-x Ru_ x O_ 2 (0x 0.5)samples remain thatin the γphaseof Na_ 0.75 CoO_ 2 . The partial substitution of Ru for Co results in a remarkable increase in resistivity for this system. For the x0 sample, the temperature dependence of resistivity, ρ(T), shows a metallic behavior in all the measuring temperature range. For the x0.01 sample, the ρ(T) relationship shows a metal-insulator (MI) transition around 37K. All the samples with x0.02 are semiconductor in all the measuring temperature range. Compared with the un-doped sample, the resistivity of x0.1 sample increases more than 5 orders in magnitude at 30 K. It is suggested that the MI transition near x0.01 in Na_ 0.75 Co_ 1-x Ru_ x O_2 system may be attribute to the Anderson electron localization in CoO_2 sheet due to the disorder. For all the Na_ 0.75 Co_ 1-x Ru_ x O_ 2 (0x 0.5)samples, no long-range magnetic order has been detected down to 2K, and the temperaturedependence of susceptibility above 100 K can be fitted using Curie-Weiss law. The susceptibility results for this system have been discussed in detail.