Water‐Mediated Synthesis of a Superionic Halide Solid Electrolyte
Xiaona Li,Jianwen Liang,Ning Chen,Jing Luo,Keegan R. Adair,Changhong Wang,Mohammad Norouzi Banis,Tsun‐Kong Sham,Li Zhang,Shangqian Zhao,Shigang Lu,Huan Huang,Ruying Li,Xueliang Sun
DOI: https://doi.org/10.1002/ange.201909805
2019-09-30
Angewandte Chemie
Abstract:To promote the development of solid‐state batteries, polymer‐, oxide‐, and sulfide‐based solid‐state electrolytes (SSEs) have been extensively investigated. However, the disadvantages of these SSEs, such as high‐temperature sintering of oxides, air instability of sulfides, and narrow electrochemical windows of polymers electrolytes, significantly hinder their practical application. Therefore, developing SSEs that have a high ionic conductivity (>10−3 S cm−1), good air stability, wide electrochemical window, excellent electrode interface stability, low‐cost mass production is required. Herein we report a halide Li+ superionic conductor, Li3InCl6, that can be synthesized in water. Most importantly, the as‐synthesized Li3InCl6 shows a high ionic conductivity of 2.04×10−3 S cm−1 at 25 °C. Furthermore, the ionic conductivity can be recovered after dissolution in water. Combined with a LiNi0.8Co0.1Mn0.1O2 cathode, the solid‐state Li battery shows good cycling stability. Ein superionischer Leiter, Li3InCl6, mit einer Li+‐Leitfähigkeit bei Raumtemperatur von 2.04×10−3 S cm−1 wurde über eine einfache und skalierbare wasservermittelte Route synthetisiert. Die reversible Umwandlung zwischen Li3InCl6 und Li3InCl6⋅2 H2O macht ihn stabil gegen Luft und Feuchtigkeit, was gewährleistet, dass die hohe Ionenleitfähigkeit nach der Umwandlung zurückgewonnen wird.