Hot deformation behaviors and dynamic softening mechanisms of 7Mo super-austenitic stainless steel with high stacking fault energy

Shiguang Xu,Jinshan He,Runze Zhang,Fucheng Zhang,Xitao Wang

DOI: https://doi.org/10.1016/j.jmrt.2023.01.108

IF: 6.267

2023-01-24

Journal of Materials Research and Technology

Abstract:Hot deformation behaviors and dynamic softening mechanisms of the 7Mo super-austenitic stainless steel (SASS) were studied in the temperature range of 1000∼1200 °C and stain rate of 0.001∼10 s -1 . It is found the optimum windows of hot deformation are mainly in the temperature range of 1030∼1200 °C and strain rate range of 0.001∼0.07 s -1 , and temperature range of 1050∼1200 °C and strain rate of 10 s -1 . The apparent activation energy of 7Mo SASS has reached 558.9 kJ mol -1 , which is about 100∼180 kJ mol -1 larger than ordinary austenitic stainless steels and about 60∼95 kJ mol -1 larger than 4.5∼6 wt.% Mo super-austenitic stainless steels. Due to high high stacking fault energy (SFE, 161.2 mJ m -2 ), planar gliding of dislocations is the main deformation mechanism of 7Mo SASS. As a result, dynamic recovery (DRV) and continuous dynamic recrystallization (CDRX) are easy to occur and play dominant roles in dynamic softening mechanism of this steel. In addition, at strain rate of 10 s -1 , especially at low temperature, the appearance of microbands (MBs) significantly promotes CDRX. Large initial sigma precipitates and micron-sized dynamic sigma precipitates also promote CDRX through the particle-stimulated nucleation (PSN) mechanism.

materials science, multidisciplinary,metallurgy & metallurgical engineering