All-Day Anti-Icing/Deicing Film Based on Combined Photo-Electro-Thermal Conversion

Tongtong Hao,Zhicheng Zhu,Huige Yang,Zhiyuan He,Jianjun Wang

DOI: https://doi.org/10.1021/acsami.1c13252

2021-09-09

Abstract:Solar energy-facilitated icephobic films have emerged as clean and renewable materials, which can potentially solve energy loss problems during anti-icing/deicing applications. However, there is a significant challenge for all-day and continuous anti-icing/deicing applications under practical conditions with insufficient sunlight or no sunlight. In this work, a chemical oxidation polymerization method was used to prepare in situ self-wrinkling porous poly(dimethylsiloxane) (PDMS)/polypyrrole (PPy) (POP-P) films based on a facile sugar template method. The porous-structured film enhanced light absorption by elongating the optical path for multiple reflections, maintaining an outstanding broad-band solar light absorption (295–2500 nm) and an exceptional photo-thermal effect. The light-to-heat performance showed a temperature enhancement from room temperature to 89.1 °C within 400 s under 1 sun illumination (qi = 1.0 kW m–2). In addition, this membrane also exhibited an electro-thermal effect at different voltages due to the Joule effect, and the saturation temperature could reach 75.4 °C at a voltage of 32 V. As an anti-icing/deicing material, this POP-P surface remained ice-free (−25 °C) throughout alternating of day and night, under conditions of a solar intensity of 0.8 kW m–2 and a voltage of 25 V.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c13252.Illustration of simulated ice coverage experiments with controlled solar illumination and voltage (Figure S1); preparation process of PLP-P film (Figure S2); IR images of POP-P-120 films under an illumination intensity of 1 kW m–2 (Figure S3); equilibrium temperature of the PDMS/PPy films and the temperature changing curve of PLP-P-120 and POP-P-120 under different light intensities (Figure S4); schematic illustration for the photo-thermal conversion measurements at different incident angles (Figure S5); in situ melting process of a frozen droplet on PDMS and PLP-P-120 (Figure S6); deicing experiments only using electro-thermal conversion (Figure S7); ice coverage experiments of day 1 and day 180 (Figure S8); and repeated icing/deicing cycles (Figure S9) (PDF)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology