Investigation of impact performance of 3-dimensional interlock polymer fabrics in double and multi-angle pass stabbing

Mengru Li,Peng Wang,François Boussu,Damien Soulat

DOI: https://doi.org/10.1016/j.matdes.2021.109775

2021-08-01

Abstract:<p>This paper presents the influence of fabric structures and stab angles on single-pass stab impact and the repeated and multi-angle stabbings of 3-dimensional (3D) warp interlock structural fabrics based on the high-molecular-weight polyethylene (HMWPE) yarns. Five kinds of samples with different structures were experimentally tested using the drop weight stabbing impact equipment at the same impact energy. Radar charts are plotted to demonstrate the differences among different parameters to a better understanding and a more global characterization of single-pass stabbing impact. An image analysis methodology of Structure From Motion (SFM) is used to compare the fabric deformation in Z direction after the stabbing tests. Results indicated that fabric structures have significant effects on the stab impact property that the orthogonal/through-the-thickness interlock fabric has a good stab impact resistance. Besides, the fabric with stab angle of 90° exhibited better single-pass stab impact property than the counterparts with stab angle of 0°. More importantly, the double-pass stabbing tests are compared to the ones of the single-pass stabbing which shows that a better condition occurs when the stab angles are identical in each pass.</p>

materials science, multidisciplinary

What problem does this paper attempt to address?

The problem this paper attempts to address is: studying the impact of 3D fabric structure and stabbing angle on the stab resistance performance of high molecular weight polyethylene (HMWPE) three-dimensional (3D) warp-knitted interlock structure fabrics under single stabbing, repeated stabbing, and multi-angle stabbing. Specifically, the paper explores the stab resistance performance of different 3D fabric structures under single and double stabbing through experimental testing and analysis, and proposes new testing methods to evaluate the performance of fabrics under multiple stabbings.

### Main Research Content:
1. **Impact of Fabric Structure on Traditional Single Stabbing Performance**: Investigated the stab resistance performance of different 3D fabric structures under single stabbing.
2. **Impact of Repeated and Multi-angle Stabbing**: Studied the stab resistance mechanisms of different 3D fabric structures under repeated and multi-angle stabbing.
3. **Double Stabbing Test**: Developed and analyzed the performance of 3D structured fabrics under double stabbing.
4. **Stab Resistance Performance of Orthogonal/Through-thickness Interlock Fabrics**: Investigated the superiority of orthogonal/through-thickness interlock fabrics in stab resistance performance.
5. **Impact of Stabbing Angle on Stab Resistance Performance**: Studied the impact of different stabbing angles on single stabbing performance, finding that a 90-degree stabbing angle has better stab resistance performance than a 0-degree stabbing angle.
6. **Comparison of Double Stabbing and Single Stabbing**: Compared the stab resistance performance of double stabbing and single stabbing at the same stabbing angle, finding that stab resistance performance is better when the angle of each stabbing is the same.

### Research Background:
With the increase in knife attack incidents, especially against police and the public, the demand for stab-resistant soft armor materials is gradually increasing. Traditional stab-resistant materials such as unidirectional fabrics and two-dimensional fabrics have disadvantages like poor interlayer fracture toughness, while three-dimensional (3D) fabrics, due to their good mechanical properties and structural integrity, have become the preferred materials for future personal protective equipment (PPE).

### Research Methods:
- **Experimental Materials**: Five different structures of 3D fabrics were manufactured using high molecular weight polyethylene (HMWPE) yarns.
- **Testing Methods**: A drop-weight stabbing test device was used to conduct experiments, testing the stab resistance performance of different 3D fabric structures under single and double stabbing.
- **Data Analysis**: Detailed analysis of the experimental results was conducted using radar charts and image analysis methods (Structure From Motion, SFM).

### Main Contributions:
- **Enhanced understanding of the stab resistance performance of 3D warp-knitted interlock structure fabrics**.
- **Compared the stab resistance performance of different 3D fabric structures under single stabbing**.
- **Proposed a new double and multi-angle stabbing testing method**, supplementing the deficiencies of classical stabbing testing methods.
- **Compared the results of the new double and multi-angle stabbing testing method with traditional single stabbing testing methods**.

Through these studies, the paper provides important data support for improving the design of flexible lightweight fabrics, contributing to the development of more efficient armor and personal protective equipment.