Abstract:STATEMENT OF PROBLEM: Dental cobalt-chromium (Co-Cr) alloy manufactured by selective laser melting (SLM) is not recommended for clinical applications before annealing because of excessive residual stress. However, limited information is available regarding the relationship between annealing temperature and the metal-ceramic bond properties of SLM Co-Cr alloys.PURPOSE: The purpose of this in vitro study was to investigate the effects of annealing temperature on the metal-ceramic bond properties of SLM Co-Cr alloys.MATERIAL AND METHODS: Four groups with different annealing temperatures (850 °C; 950 °C; 1050 °C; 1150 °C) were prepared by using SLM techniques. Bond strengths were measured by using a 3-point bend test; subsequently, debonded surface morphologies and elements were assessed by using a scanning electron microscopy (SEM) coupled with energy-dispersive X-ray spectroscopy (EDS). The area fraction of adherence porcelain (AFAP) value was introduced to analyze fracture characteristics. Microstructural and interfacial characteristics were characterized by SEM/EDS and X-ray diffraction analysis. The coefficient of thermal expansion (CTE) test was used to analyze thermal matching. A 1-way ANOVA and the Tukey honestly significant difference tests were used to analyze bond strengths and AFAP values statistically (α=.05).RESULTS: The mean ±standard deviation values of the metal-ceramic bond strengths were 40.68 ±4.34 MPa for the 850 °C group, 37.54 ±5.34 MPa for the 950 °C group, 45.97 ±2.18 MPa for the 1050 °C group, and 50.79 ±1.79 MPa for the 1150 °C group. Significant differences (P<.05) were observed among all groups. Debonded surfaces and AFAP analysis displayed a mixed fracture mode of adhesive and cohesive fracture, and 1150 °C-annealing specimens exhibited better fracture characteristics close to cohesive fractures. As the temperature increased, native oxide film thicknesses remained unchanged; the 850 °C group had the thinnest diffusion layer, while the other 3 groups had similar thicknesses. Although the 1050 °C and 1150 °C groups displayed higher CTE values, their microstructures were more conducive to atomic diffusion and improved chemical bonding. Microstructure analysis found that ε phase and second-phase precipitates jointly affected metal-ceramic bond strength.CONCLUSIONS: Annealing temperatures affected the metal-ceramic bond strengths of SLM Co-Cr porcelain specimens. 1150 °C annealing SLM Co-Cr specimens displayed higher bond strengths and improved fracture and interface characteristics among the 4 groups.

The effect of cooling rate on the apparent bond strength of porcelain-metal couples

Effects of extreme cooling methods on mechanical properties and shear bond strength of bilayered porcelain/3Y-TZP specimens

[Effect of the treatments preceding porcelain baking on the strength of the ceramic-metal bond]

Effect of cooling rate on hardness and microstructure of Pd-Ag-In-Sn-Ga alloy during porcelain firing simulation

Strength of 3Y-TZP and feldspathic porcelain subjected to different cooling methods

Effects of posttreatment on the metal-ceramic bond properties of selective-laser-melted Co-Cr dental alloy—Part 2: Heat treatment after porcelain firing

Surface preparation for orthodontic bonding to porcelain

Effect of rapid cooling on residual stress and surface fracture toughness of dental zirconia

Extended glaze firings for porcelain-veneered zirconia: Effects on the mechanical and optical behavior

X-Ray diffraction and scanning electron microscopy-energy dispersive spectroscopic analysis of ceramõmetal interface at different firing temperatures

Effects of post-treatment on metal-ceramic bond properties of selective laser melted Co-Cr dental alloy. Part 1: Annealing temperature

Effect of TiO2–SiO2 sol–gel coating on the cpTi–porcelain bond strength

Bond strengths of porcelain to cobalt-chromium alloys made by casting, milling, and selective laser melting

Wettability and Bond Strength Between Leucite-Reinforced Dental Porcelains and Co-Cr Alloy.

Effect of multiple firings on the shear bond strength of presintered cobalt-chromium alloy and veneering ceramic

Hardening by cooling rate control and post-firing heat treatment in Pd-Ag-Sn alloy for bonding porcelain

The possibility of clinical bonding between metal/ceramic brackets to zirconia: in vitro study

Effect of oxidation heat treatment on the bond strength between a ceramic and cast and milled cobalt-chromium alloys

[The shear bond strength of porcelain and base metal alloys for metal-ceramic crown (VII)]

Evaluation of Microtensile Bond Strength Between Resin Composite and Glass Ceramic

The effect of long-term water storage on the resin adhesive interface between dentine and glass ceramic