Preparing Porous Calcium Hexaluminate (CA6) Ceramics with Calcium Aluminate Cement (CAC) As the Gelling Agent and Sole Calcia Source

Haiyang Lu,Yanjun Li,Donghua Liu,Jiashen Wen,Daofeng Sun,Endong Jin,Jin Chen,Donghai Ding,Guoqing Xiao

DOI: https://doi.org/10.1016/j.jallcom.2024.177625

IF: 6.2

2024-01-01

Journal of Alloys and Compounds

Abstract:Porous calcium hexaluminate (CA6) is attractive for thermal insulation due to low conductivity and chemical stability at high temperatures. In this study, porous CA6 ceramics were fabricated by a direct foaming method using calcium aluminate cement (CAC) as a gelling agent and sole calcia source. The results showed that the firing temperature is a significant factor in forming the CA6. In the samples fired at 1550 and 1650 °C, the main phase was CA6. Especially for samples fired at 1650 °C, the CA6 content was as high as 90%. With the firing temperature increased, the compressive strength of the sample using tabular alumina and high-pure ultra-fine alumina was increased significantly, while the size of foamed spherical pores was decreased. In addition to the firing temperature, the type of raw alumina plays a key role in forming the CA6. The sample using high-pure ultra-fine alumina exhibited commendable comprehensive properties. The compressive strength is 5.12MPa, and the thermal conductivity is 0.46W·m-1·K-1. The work exhibited a simple process for producing porous CA6 ceramic with high porosity and commendable properties, including thermal insulation and compressive strength, using CAC as a gelling agent and sole calcia source.