Abstract:In this paper, the workability, mechanical, ion leaching, and drying shrinkage properties of alkali-activated concrete with recycled coarse and fine aggregates were studied, and the pore structure and micro-morphology of different alkali-activated recycled aggregate concretes (AARACs) were characterized by using the mercury intrusion method and scanning electron microscopy, respectively. The experimental results showed that with the increase in the replacement rate of the recycled fine aggregate (RFA), the flowability showed a decreasing trend. Adding a certain amount of RFA improves the mechanical properties of the AARAC. The compressive strength at a curing age of 28 days was 65.3 MPa with 70 wt% RFA replacement. When the replacement rate of the RFA was 100 wt%, the maximum splitting tensile strength (4.5 MPa) was obtained at a curing age of 7 days. However, the addition of the RFA had little effect on the flexural strength of the AARAC. As an extension of the curing age, the splitting tensile strength, flexural strength, tension-to-compression ratio, and flexure-to-compression ratio all showed an increasing trend at first and then a decreasing trend. At a curing age of 7 days, the tension-to-compression ratio and flexure-to-compression ratio were both high (except for those of R100), indicating that the ductility and toughness of the specimen were improved. The addition of the RFA increased the drying shrinkage of the AARAC. At a curing age of 120 days, compared to the specimen without the RFA, the drying shrinkage rate of the specimen with the addition of 70 wt% RFA increased by 34.15%. As the curing age increased, the microstructure of the reaction products became denser, but the proportion of large-diameter pores increased. This study evaluated the application of RFA in AARAC. The experimental results showed that the RFA-based AARAC had acceptable mechanical and durability properties.

Mechanical Properties and Early-Age Shrinkage of Ultra-High Performance Concrete Mortar with Recycled Fine Aggregate

Powder Gradation Effect on the Fresh, Mechanical, and Early-Age Shrinkage Properties of UHPC

Sustainable Use of Recycled Autoclaved Aerated Concrete Waste As Internal Curing Materials in Ultra-High Performance Concrete

Investigation of Mechanical Properties of Ultra-High-Performance Polyethylene-Fiber-Reinforced Recycled-Brick-Aggregate Concrete

Shrinkage Mitigation of an Ultra-High Performance Concrete Submitted to Various Mixing and Curing Conditions

Internal Curing Effect of Saturated Recycled Fine Aggregates in Early-Age Mortar

Influence of Hybrid Fiber Reinforcement on Mechanical Properties and Autogenous Shrinkage of an Ecological UHPFRCC

Drying Shrinkage of Mortar Manufactured with Recycled Fine Aggregate at Vary Initial Saturation Degree

Effect of Ultra-Fine Fly Ash on the Mechanical and Shrinkage Properties of Ultra-High Performance Concrete

Using Limestone Calcined Clay Cement and Recycled Fine Aggregate to Make Ultra-High-performance Concrete: Properties and Environmental Impact

Effects of Shrinkage Reducing Agent and Expanded Cement on UHPC Fluidity, Mechanical Properties, and Shrinkage Performance

Application of Sisal Fiber Powder in Ultra-High Performance Concrete: A Renewable Material for Mitigating Autogenous Shrinkage

Effect of Recycled Fine Aggregates on the Mechanical and Drying Shrinkage Properties of Alkali-Activated Recycled Concrete

Autogenous shrinkage and nano-mechanical properties of UHPC containing waste brick powder derived from construction and demolition waste

An alternative method for performance improvement of ultra-high performance concrete by internal curing: Role of physicochemical properties of saturated lightweight fine aggregate

Durability and shrinkage performance of self-compacting concrete containing recycled fine clay brick aggregate

Mechanical Properties and Shrinkage of Ultrahigh-Performance Concrete Containing Lithium Carbonate and Nano-Calcium Carbonate

Long-term shrinkage and mechanical properties of fully recycled aggregate concrete: Testing and modelling

Mechanical Performance and Microstructure of Ultra-High-Performance Concrete Modified by Calcium Sulfoaluminate Cement

Plastic and early-age shrinkage of ultra-high performance concrete (UHPC): Experimental study of the effect of water to binder ratios, silica fume dosages under controlled curing conditions

Experimental Study and Analytical Modeling of Tensile Performance of Ultra-High-Performance Concrete Incorporating Modified Recycled Aggregates