Abstract:Biobased thermosetting polymers have attracted interest owing to their renewable source materials, long service life, and properties comparable to those of petroleum-based materials. However, the fabrication of those that merge exquisite mechanical properties with fast self-healing performance has not been demonstrated to date. In this work, a biobased polyurethane coating was constructed using curcumin dioxime (CD), castor oil (CO), and isophorone diisocyanate (IPDI) to fulfill these features. The biobased CD monomer was prepared using curcumin and hydroxylamine hydrochloride and confirmed by nuclear magnetic resonance, flourier-transform infrared (FT-IR) spectra, and high-resolution mass spectrometry (HR-MS). To investigate the correlation between the mechanical properties and self-healing performance, a series of polyurethane coatings were fabricated by varying the ratio of CO to CD. The results showed that the crosslinking density ( v e ), glass transition temperature ( T g ), and Young modulus of these coatings increased with the decrease in the ratio of CO to CD, leading to tunable mechanical properties. In particular, the tensile strength and elongation of the COPU-4 coating were as high as 17.2 MPa and 295 %, respectively. The stress relaxation experiments revealed that these coatings exhibited low activation energy ( Ea ), as low as 28.3 kJ/mol for COPU-5. Besides, all COPU-X coatings demonstrated self-healing efficiency higher than 71 % within 1 min at 90 °C, and some of them even reached >90 % after 8 min. The results demonstrate the promising tunable mechanical and excellent self-healing properties of these novel biobased polyurethane coatings and pave the way for the development of bioderived sustainable thermosetting polymers.

Design and Synthesis of UV-cured Calixarene Polyurethane Coatings: Balancing Robust Mechanical Properties with High Self-Healing Efficiency

Properties of UV-cured Self-Healing Coatings Prepared with PCDL-based Polyurethane Containing Multiple H-bonds

Self-Healing Polyurethane-Urea Elastomers with High Strength and Toughness Based on Dynamic Hindered Urea Bonds and Hydrogen Bonds

Mechanically Robust and Self-Healable Polyureas Based on Multiple Dynamic Bonds

Designed Preparation of Silicone Protective Materials with Controlled Self-Healing and Toughness Properties

A High‐performance Self‐healing Polyurea Material Based on Exchangeable Aromatic Disulfide

Designing an elastomeric polyurethane coating with enhanced mechanical and self-healing properties: The influence of disulfide chain extender

Robust Self‐healing Waterborne Polyurethane Coatings Via Dynamic Covalent Diels‐Alder Bonds for Corrosion Protection

UV-curable self-healing, high hardness and transparent polyurethane acrylate coating based on dynamic bonds and modified nano-silica

Synthesis of robust and self-healing polyurethane/halloysite coating via in-situ polymerization

Biobased polyurethane coatings with fast self-healing and tunable mechanical properties derived from curcumin and castor oil

Multifunctional Polyurethane Coatings with Excellent Antifouling and Self-Healing Properties

Main‐Side Chain Hydrogen Bonding‐Based Self‐Healable Polyurethane with Highly Stretchable, Excellent Mechanical Properties for Self‐Healing Acid–Base Resistant Coating

Preparation of multi band photothermal responsive bio-based superhydrophobic self-healing poly(siloxane-urethane) coating

A High Stiffness and Self-Healable Polyurethane Based on Disulfide Bonds and Hydrogen Bonding

Preparation and Properties of Self-healing Microcapsules Containing an UV-curable Oligomers of Silicone

UV‐curable Polyurethane Elastomer with UV‐irradiation/Thermo Dual‐Activated Self‐healability

Synthesis and Characterization of Poly(Urea-Formaldehyde) Microcapsules Containing Linseed Oil for Self-Healing Coating Development

A Tough Polyurethane Elastomer with Self-Healing Ability

Diels-Alder-Based Crosslinked Self-Healing Polyurethane/Urea from Polymeric Methylene Diphenyl Diisocyanate

Role of Diisocyanate Structure on Self‐Healing and Anticorrosion Properties of Waterborne Polyurethane Coatings