Abstract:We synthesized a self-healing polyurethane elastomer (PU-SSDA) which displayed excellent healing efficiency at room temperature due to the synergistic contribution of dynamic covalent D-A bond and S-S bond. Mechanical and self-healing properties of the polyurethane elastomers were characterized by tensile test and three-dimensional super depth of field microscope. The cross-linking structure of PU-SSDA is explored by extraction experiments, demonstrating that there are not only crosslinked structures but also linear molecular segments existed in the polyurethane elastomer. Mechanical properties of the PU-SSDA elastomer can be tuned by changing the cross-linking degree. As the crosslinking degree increases from 25% to 45%, the tensile strength increases from 2.9 MPa to 5.5 MPa while the elongation at break decreases from 795% to 304%. After optimization, when the crosslinking degree was 35%, the tensile strength was 3.7 MPa, the elongation at break was 606% and the repair efficiency could be restored to 93% after healing for 60 min at room temperature. Moreover, the healing efficiency still remains above 90% after 4 damage-healing cycles. In addition, the PU-SSDA elastomer can also be reprocessed by hot pressing at 120 degrees C. This excellent self-healing behavior and reprocessable property were attributed to the reversible fracture recombination reaction of dynamic D-A and S-S bonds and the quick infiltration of the linear polymer chains into damaged surface. The self-healing mechanism can be further confirmed by the dissolution experiments which showed that the PU-SSDA elastomer can be dissolved in DMF at 100 degrees C while the PU-control can only swell under the same conditions, demonstrating that the reversible cleavage and reformation of D-A and S-S bonds contribute a lot to the self-healing process. Due to the facile and friendly preparation method, fast self-healing behavior at room temperature and fully reprocessable properties, the as prepared polyurethane elastomers displayed wide potential applications such as protection coatings and wearable electronic devices.

Diels-Alder-Based Crosslinked Self-Healing Polyurethane/Urea from Polymeric Methylene Diphenyl Diisocyanate

Polyether–maleimide‐based Crosslinked Self‐healing Polyurethane with Diels–Alder Bonds

Self-Healing Polyurethane-Urea Elastomers with High Strength and Toughness Based on Dynamic Hindered Urea Bonds and Hydrogen Bonds

Synthesis and Characterization of Linear Self-Healing Polyurethane Based on Thermally Reversible Diels–Alder Reaction

A High‐performance Self‐healing Polyurea Material Based on Exchangeable Aromatic Disulfide

Slightly Crosslinked Polyurethane with Diels–Alder Adducts from Trimethylolpropane

Thermal- and Mechanical-Responsive Polyurethane Elastomers with Self-Healing, Mechanical-Reinforced, and Thermal-Stable Capabilities

Properties of UV-cured Self-Healing Coatings Prepared with PCDL-based Polyurethane Containing Multiple H-bonds

Synthesis and Properties of Thermally Self-Healing PET Based Linear Polyurethane Containing Diels-Alder Bonds

Preparation of Living and Highly Stable Blended Polyurethane Emulsions for Self-Healing Films with Enhancive Toughness and Recyclability

Polybutadiene Derived Allophanate As the Crosslinker for Diels–Alder Type Self‐healing Polyurethane Networks

Coordination Bonds And Diels-Alder Bonds Dual Crosslinked Polymer Networks Of Self-Healing Polyurethane

Robust, stretchable and photothermal self-healing polyurethane elastomer based on furan-modified polydopamine nanoparticles

Polyurethane-based crosslinked polymer with tunable self-healable and mechanical properties

Super‐Tough, Self‐Healing Polyurethane Based on Diels‐Alder Bonds and Dynamic Zinc–Ligand Interactions

Room-temperature Self-healable and Reprocessable Polyurethane Elastomers Combined Diels-Alder Bond and Disulfide Bond

Multi-responsive self-healing behavior of polyurethane modified with photothermal and microwave conversion nanoparticles

Self-healing Polyurethane Elastomer with Thermally Reversible Alkoxyamines As Crosslinkages

A Tough Polyurethane Elastomer with Self-Healing Ability

Self-Healing Polyurethanes Based on Natural Raw Materials

Self-Healing and Recyclable Polyurethane/Nanocellulose Elastomer Based on the Diels-Alder Reaction