Tuning of the Mechanical Properties of a Laser Powder Bed Fused Eutectic High Entropy Alloy Ni30Co30Cr10Fe10Al18W2 Through Heat Treatment

Yiwei Yu,Yakai Zhao,Kai Feng,Rong Chen,Bolun Han,Kaifeng Ji,Meng Qin,Zhuguo Li,Upadrasta Ramamurty

DOI: https://doi.org/10.1016/j.msea.2024.147469

2024-01-01

Abstract:Eutectic high entropy alloys (EHEA) with an exceptional combination of strength and ductility are promising candidates as advanced structural materials. However, achieving an optimal balance between the properties in additively manufactured EHEAs is an outstanding challenge. In this work, Ni30Co30Cr10Fe10Al18W2 EHEA was additively manufactured using the laser powder bed fusion (LPBF) technique. In the as-fabricated state, it exhibits a dual-phase nano-lamellar structure consisting of FCC/L12 and B2 phases. Post-fabrication heat treatments were explored for modulating microstructure and, in turn, enhancing the mechanical properties, so as to achieve an optimum balance between strength and ductility. Upon heat treatment at 750 degrees C for 1 h, part of the B2 phase transformed into FCC, with the appearance of the tungsten-rich precipitates inside the B2 phase. The average interlayer spacing of the FCC/L12 lamellae increased to 124 nm, while that of B2 lamellae decreased to 86 nm, resulting in an alloy with an ultimate tensile strength (UTS) of 1811 MPa, although the strain to failure (epsilon f) decreased to 2 %. Upon increasing the heat treatment temperature to 1000 degrees C, the average interlayer spacings of the FCC and B2 phases increased to 210 and 187 nm, respectively, which resulted in a more balanced mechanical behavior with UTS and epsilon f of 1332 MPa and 9.3 %, respectively. This study provides an effective approach for microstructural modulation and enhancement of mechanical properties of LPBF fabricated EHEA via post-fabrication heat treatment, offering insights for developing future high-performance alloys for advanced structural applications.