Organic pollutants photodegradation increment with use of TiO 2 nanotubes decorated with transition metals after pulsed laser treatment
Zuzanna Bielan,Adam Kubiak,Jakub Karczewski,Jacek Ryl,Karol Załęski,Emerson Coy,Piotr Krawczyk,Katarzyna Siuzdak
DOI: https://doi.org/10.1016/j.mssp.2024.108378
IF: 4.1
2024-04-05
Materials Science in Semiconductor Processing
Abstract:Among various titanium(IV) oxide (TiO 2 , titania) structures, 1D nanotubes (TiO 2 NTs) produced during the two-electrode anodization process, are extensively utilized in sensors or supercapacitors as well as in photo(electro)catalytic water splitting. However, due to wide bandgap and fast electron-hole recombination additional modifications, mostly concerned on materials surface, are required. According to the recent research, TiO 2 NTs photo(electro)catalytic characteristic were markedly improved by the combination of surface decoration with transition metal nanoparticles further treated with the laser beam. Nevertheless, until recently, the photocatalytic ability of laser-treated TiO 2 NTs for recalcitrant chemicals degradation were hardly described. In this regard, our work focuses on obtaining long, about 7.3 μm TiO 2 NTs (L-TiO 2 NTs), together with their photoactivity and physicochemical characteristics, as well as their alterations following surface modification utilizing transition metals (tungsten, chromium and nickel) together with laser treatment. Obtained L-TiO 2 NTs are characterized by over 13.5 times larger BET surface area in comparison to reference spaced TiO 2 NTs with approximately 2 μm length (0.61 m 2 g −1 and 0.05 m 2 g −1 , respectively). This allowed for increasing of the materials photocatalytic activity in both UV–vis and vis light. Additionally, phenol photodegradation reached up to 34% (0.21·10 −2 min −1 ) for tungsten-modified titania after laser annealing at 20 mJ cm 2 fluence. The reaction mechanism research revealed that reduction of organic pollutants concentration was primarily caused by superoxide radical anions • O 2 − . Furthermore, obtained modified L-TiO 2 NTs showed remarkable durability without losing their initial activity over ten photocatalytic cycles.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied