Effect of Precursor Microstructure on Retained Austenite and Mechanical Property of Low Carbon Steels with Iq&P Treatments
Chen Lian-sheng,Hu Bao-jia,Song Jin-ying,Zhang Jian-yang,Zheng Xiao-ping,Wei Ying-li,Tian Ya-qiang
DOI: https://doi.org/10.13374/j.issn2095-9389.2016.02.010
2016-01-01
Abstract:The effects of pretreated microstructure on the multiphase microstructure features at room temperature and the mechani-cal properties of low-carbon steel were studied by the treatment of water cooling after hot-rolling in the γ phase region or in the γ+αphase region followed by the treatment of intercritical reheating-quenching-partitioning ( IQ&P) . Two different pretreated microstruc-tures, which are martensite and martensite + ferrite, are obtained by the two different hot-rolling and quenching processes. After IQ&P, the steel with martensite as pretreated microstructure, in which the volume fraction of retained austenite is 8. 2%, is turned into a multi-phase structure composed of lath intercritical ferrite, block tempered martensite, needle-like untempered martensite, and retained austenite. While the steel with martensite + ferrite as pretreated microstructure, in which the volume fraction of retained austenite is 14. 3%, is turned into a multi-phase structure composed of lath intercritical ferrite, block or needle-like untempered martensite, and short needle-like or block retained austenite. With the same IQ&P process parameters, the tensile strength of the steel with martensite as pretreated microstructure is 770 MPa, the elongation is 28%, and the product of strength and elongation is 21560 MPa·%. While the tensile strength of the steel with martensite + ferrite as pretreated microstructure is 834 MPa, the elongation increases to 36. 2%, and the product of strength and elongation reaches to 30190 MPa·%. In other words, the steel has obtained a good combination of strength and ductility.