A Strong, Ductility Maintained, and High-Temperature Resistant Ti-based Composite with TiC@(TiCr2+α-Ti) Reinforced Particles

Hongjie Wang,Zhenying Huang,Xue Li,Qun Yu,Wenqiang Hu,Weici Zhuang
DOI: https://doi.org/10.1016/j.jallcom.2024.176892
IF: 6.2
2024-01-01
Journal of Alloys and Compounds
Abstract:While material with light, strong, and high-temperature environment resistant is highly attractive to aeroengines, achieving the combination of all these properties in composite remains a challenge. As these properties typically require the combination of various materials, especially incorporating the extremely brittle intermetallic compound at room temperature into a particle-reinforced composite inherently troubled by the "strength-ductility" contradiction, which can easily exacerbate the inherent brittleness of the material. Herein, we present a composite based on Cr2AlC-Ti system, which generates reinforcements with TiC@(TiCr2+alpha-Ti) shell-core architecture in the Ti matrix through a straightforward eutectoid reaction. The reinforcements are continuously distributed on a macroscopic level, establishing a co-continuous structure with beta-Ti in 3D space. Microscopically, the shell-core structure has a multi-level TiCr2/alpha-Ti alternating layer structure as in natural nacre. This multiscale and multi-level structural design overcomes the brittleness of TiCr2 at room temperature by controlling its morphology and distribution, and achieves high content of ceramic particles in composite. The resulting composite has a compressive strength of about 2 GPa at room temperature, and even at 600 degrees C when Ti matrix is completely softened, the composite has a commendable strength of about 800 MPa.
What problem does this paper attempt to address?