Abstract:Superlubricity, a cutting-edge concept, has the potential to drive the Fourth Industrial Revolution giving its near-zero energy consumption, but the challenge is how to achieve it in humid air with chemical activity and at macroscale surfaces with unavoidable defects. Here, a novel principle involving the amorphous/crystalline friction pair based on the cognition that tribochemical interaction sites originate from grain boundary defect locations is proposed to achieve macroscale superlubricity in humid air. The absence of grain boundaries in amorphous diamond-like carbon (DLC) significantly reduces chemical interaction during the sliding process. This is supported by experimental observations of priority oxidation at the grain boundaries. Results indicate DLC versus MoS2 friction pair has weakened chemical interaction and less humid insensitivity compared to the MoS2 versus MoS2 pair, even increasing the contact area. Theoretical simulation suggests that DLC versus MoS2 pair eliminates the cross-linking of friction interlayers induced by the enrichment of H2O molecules at MoS2 defects. The robust superlubricity is achieved for the typical friction pair of DLC versus MoS2 in air (RH <= 25%) at macroscopic contact pressure (1.1 GPa) with friction coefficient in 10-3 magnitude and extra-long anti-wear life (more than 2 x 105 cycles), which is of significance for the industrialization of superlubricity. Here, a novel principle involving the amorphous lubricants/crystalline lubricants friction pair based on the cognition that tribochemical interaction sites originate from grain boundary defect locations is proposed to achieve macroscale superlubricity in humid air. image

Macroscopic Superlubricity Achieved by Hydrolysis Reaction of Ethyl Lactate on Silicon-doped Diamond-like Carbon Film

3-Hydroxypropionic Acid Triggers Macroscopic Superlubricity on the Diamond-Like Carbon Film

Polyethylene Glycol Monolaurate Lubrication Triggers Liquid Superlubricity on Diamond-like Carbon Film

Genesis of Superlow Friction in Strengthening Si-DLC/PLC Nanostructured Multilayer Films for Robust Superlubricity at Ultrahigh Contact Stress.

Macroscale Superlubricity of Si-doped Diamond-Like Carbon Film Enabled by Graphene Oxide As Additives

Lithium Citrate Triggered Macroscopic Superlubricity with Near-Zero Wear on an Amorphous Carbon Film

Design architecture of colorful Si-DLC/PLC nanostructured multilayer films for robust superlubricity at high contact stress in dry N2 atmosphere

Robust Macroscale Superlubricity in Humid Air Via Designing Amorphous DLC/Crystalline TMDs Friction Pair

Enhanced superlubricity on a-C films by lubrication with 3-hydroxypropionic acid

Shear-induced interfacial reconfiguration governing superlubricity of MoS2-Ag film enabled by diamond-like carbon

Graphitic Encapsulation and Electronic Shielding of Metal Nanoparticles to Achieve Metal-Carbon Interfacial Superlubricity.

Durable superlubricity of hydrogenated diamond-like carbon film against different friction pairs depending on their interfacial interaction

Macroscopic Superlubricity Achieved by Polyacrylic Acid Modified Fe3o4 Nanoparticles As Additives

Alkyl-functionalized black phosphorus nanosheets triggers macroscale superlubricity on diamond-like carbon film

Mechanism of superlubricity of a DLC/Si3N4 contact in the presence of castor oil and other green lubricants

100 Km Wear-Free Sliding Achieved by Microscale Superlubric Graphite/dlc Heterojunctions under Ambient Conditions

Unraveling the Friction Evolution Mechanism of Diamond‐Like Carbon Film during Nanoscale Running‐In Process toward Superlubricity

Influence Factors on Mechanisms of Superlubricity in DLC Films: A Review

DLC and Glycerol: Superlubricity in Rolling/Sliding Elastohydrodynamic Lubrication

Macroscale Superlubricity Enabled by Rationally Designed MoS2-based Superlattice Films

Tribochemical mechanism of superlubricity in graphene quantum dots modified DLC films under high contact pressure