Durable superlubricity of hydrogenated diamond-like carbon film against different friction pairs depending on their interfacial interaction

Yunhai Liu,Yilong Jiang,Junhui Sun,Lei Wang,Yangqin Liu,Lei Chen,Bin Zhang,Linmao Qian

DOI: https://doi.org/10.1016/j.apsusc.2021.150023

IF: 6.7

2021-09-01

Applied Surface Science

Abstract:<p>Superlubricity of hydrogenated diamond-like carbon (H-DLC) film in vacuum was achieved against four different friction pairs (ZrO₂, Al₂O₃, Si₃N₄ and SiC) due to the formation of graphene and nanoscrolls in transfer layer as well as the graphitization of contacted substrate; however, the durability of superlubricity was significantly diverse. The Al₂O₃/H-DLC pair presents much longer superlubricity lifetime than other three tribology systems. Combining with the experimental characterizations and the first principles calculation results, the synergistic effects from mechanical action and interfacial adhesion interaction between two sliding surfaces were found to mainly respond to the superlubricity failure of H-DLC films. High mechanical action or/and strong interfacial adhesion interaction facilitated the wear of counterface or H-DLC substrate, either of which would largely weaken the durability of superlubricity. Through with the similar mechanical action compared to the Si₃N₄/H-DLC interface, the Al₂O₃/H-DLC interface was capable of durable superlubricity since the much weaker interfacial adhesion interaction helps maintain the stable transfer layer on the ball surface and form smoothly graphitized substrate surface in the contacted region.</p>

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films