Thermal Stable NaMgLaTeO6:Dy3+ Double Perovskite Yellow Phosphors for W-Leds and Latent Fingerprint Visualization

Xinjing Xie,Yangyang Tuo,Siyu Cheng,Di Gao,Mengkun Zhang,Xiang Liu,Huajuan Deng,Ruijin Yu

DOI: https://doi.org/10.1016/j.materresbull.2024.113098

IF: 5.6

2025-01-01

Materials Research Bulletin

Abstract:The novel Dy3+-doped NaMgLaTeO6 (NaMgLaTeO6:Dy3+) phosphors were produced through a high-temperature solid-state reaction. X-ray diffraction (XRD) analysis and Rietveld refinement manifest that the pure phosphor was committed to the space group (P2(1/m) (11)) and features the double perovskite structure. The band gap (E-g) of the direct semiconductor NaMgLaTeO6 is calculated to be 2.065 eV. Under 388 nm excitation, the F-4(9/2)-> H-6(13/2) energy level transition contributes to the maximum emission peak at 572 nm. Other properties of the phosphor include optimal concentration (x = 5 mol %), high thermal stability, activation energy (E-a = 0.31 eV), and internal quantum efficiency (IQE = 31.44 %). The relevant color coordinate of the white light emitting diode (w-LED) prepared by the phosphor is (0.298, 0.311). The features of the latent fingerprint (LFP) created by NaMgLaTeO6:Dy3+ can be clearly reflected on different surfaces. In summary, NaMgLaTeO6:Dy3+ phosphor has proven high potential in w-LEDs production and LFP detection.