Yellow Emission Obtained By Combination Of Broadband Emission And Multi-Peak Emission In Garnet Structure Na2ymg2v3o12: Dy3+ Phosphor

Weiyi Zhang,Can He,Xiaowen Wu,Ximing Huang,Fankai Lin,Yan'Gai Liu,Minghao Fang,Xin Min,Zhaohui Huang

DOI: https://doi.org/10.3390/molecules25030542

IF: 4.6

2020-01-01

Molecules

Abstract:The fabrication and luminescent performance of novel phosphors Na2YMg2V3O12:Dy3+ were investigated by a conventional solid-state reaction method. Under near-UV light, the Na2YMg2V3O12 host self-activated and released a broad emission band (400-700 nm, with a peak at 524 nm) ascribable to charge transfer in the (VO4)(3-) groups. Meanwhile, the Na2YMg2V3O12:Dy3+ phosphors emitted bright yellow light within both the broad emission band of the (VO4)(3-) groups and the sharp peaks of the Dy3+ ions at 490, 582, and 663 nm at a quenching concentration of 0.03 mol. The emission of the as-prepared Na2YMg2V3O12:Dy3+ phosphors remained stable at high temperatures. The obtained phosphors, commercial Y2O3:Eu3+ red phosphors, and BaMgAl10O17:Eu2+ blue phosphors were packed into a white light-emitting diode (WLED) device with a near-UV chip. The designed WLED emitted bright white light with good chromaticity coordinates (0.331, 0.361), satisfactory color rendering index (80.2), and proper correlation to a color temperature (7364 K). These results indicate the potential utility of Na2YMg2V3O12:Dy3+ phosphor as a yellow-emitting phosphor in solid-state illumination.