Effects of retrogression and re-aging treatment on precipitation behavior, mechanical and corrosion properties of a Zr+Er modified Al-Zn-Mg-Cu alloy
Huilong Zhong,Shengci Li,Jiali Wu,Hongling Deng,Jiqiang Chen,Na Yan,Zixin Chen,Liangbo Duan
DOI: https://doi.org/10.1016/j.matchar.2021.111617
IF: 4.537
2022-01-01
Materials Characterization
Abstract:The microstructure, mechanical properties, and corrosion resistance of a Zr + Er modified Al-Zn-Mg-Cu alloy after different retrogression and re-aging (RRA) treatments were investigated. Results show that the main precipitates after different heat treatment change from GP zones + η’ + Al3(Er, Zr) phase (T6) to η’ + Al3(Er, Zr) phase (RRA180–30) and then to η + T phase (RRA200–30). The component, size, and distribution of precipitated phases would be affected by the regression time and temperature during RRA treatment. It is concluded that the uniformly dispersed precipitate phase in matrix and narrow precipitate-free zones (PFZs) could significantly improve the strength of Al-Zn-Mg-Cu alloy, and the grain boundary precipitated phase (GBPs) with moderate size and large interparticle distance could improve the alloy's corrosion resistance. Besides, a wider PFZ within a certain range is beneficial to improve the intergranular corrosion (IGC) performance. Therefore, it is important to accurately control the heating temperature and retrogression time during the retrogression stage to regulate the characteristics of precipitated phases and achieve the best balance of mechanical properties and corrosion resistance.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing