Abstract:This paper addresses the study of the complex effect of alloying elements (magnesium, manganese, copper and zirconium) on changes in magnesium-rich aluminum alloy composition, fine and coarse particle size and number, recrystallization characteristics and mechanical properties. The data obtained made it possible to analyze change in the chemical composition, sizes of intermetallic compounds and dispersoids depending on alloying elements content. The effect of the chemical composition on the driving force and the number of recrystallization nuclei was studied. It was established that the addition of alloying elements leads to grain refinement, including through the activation of a particle-stimulated nucleation mechanism. As a result, with Mg increase from 4 to 5%, addition of 0.5% Mn and 0.5% Cu, the grain size decreased from 72 to 15 µm. Grain refinement occurred due to an increase in the number of particle-stimulated nuclei, the number of which at minimal alloying rose from 3.47 × 1011 to 81.2 × 1011 with the maximum concentration of Mg, Mn, Cu additives. The retarding force of recrystallization, which in the original alloy was 1.57 × 10-3 N/m2, increased to 5.49 × 10-3 N/m2 at maximum alloying. The influence of copper was especially noticeable, the introduction of 0.5% increasing the retarding force of recrystallization by 2.39 × 10-3 N/m2. This is due to the fact that copper has the most significant effect on the size and number of intermetallic particles. It was established that strength increase without ductility change occurs when magnesium, manganese and copper content increases.

Effect of Addition Temperature on Dispersion Behavior and Grain Refinement Efficiency of MgO Introduced into Mg Alloy

Effect of Ti Addition on the Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn Alloys

Effect of Al addition on the grain refinement and mechanical properties of as-cast Mg–5Y–4Sm alloys

Heat treatment, microstructure and mechanical properties of a Mg-Gd-Y alloy grain-refined by Al additions

Mechanism of grain refinement and growth for the continuous alumina fibers by MgO addition

Comparative Studies of Grain Refinement of Commercial Purity Mg by CaO and Ca Addition

Enhancing the Mechanical Properties of Mg–Al Alloy by Introducing Al2Y Nanoparticles Via Rapid-Cooling Solidification and Optimized Heat Treatments

Effects of Heating Temperature on Partial Remelting Microstructure of AZ91D Magnesium Alloy

Effect of grain size distribution and texture on the cold extrusion behavior and mechanical properties of AZ31 Mg alloy

Effect of Al additions on grain refinement and mechanical properties of Mg–Sm alloys

Grain Coarsening Behavior of Mg-Al Alloys with Mischmetal Addition

Effects and Mechanism of Ca on Refinement of AZ91D Alloy

The Effect of Ti Addition on Microstructure Evolution of Az61 Mg Alloy During Mechanical Milling

Effect of Solution Temperature on Grain Size in A Mg-4y-3nd-3dy-0.5zr Alloy

Microstructure refinement and mechanical properties enhancement of Mg Al alloys via a novel of MgO nanoparticles modified graphene nanoplates refiner by in-situ synthesis

On Grain Coarsening and Refining of the Mg–3Al Alloy by Sm

The Effect of Cooling Rate on the Microstructure and Mechanical Properties of Mg–Zn–Gd-based Alloys

Alloying Elements Effect on the Recrystallization Process in Magnesium-Rich Aluminum Alloy

Influences of Mg content on the microstructures and mechanical properties of cast Al–2Li–2Cu–0.2Zr alloy

Al-CeO2-Mg refiner on grain refinement, cast fluidity and mechanical properties of AZ91 alloy

Effect of Grain Size on the Microstructure and Mechanical Properties of Mg-4Y-3Nd-0.5Zr Alloy