Abstract:Microstructure, texture evolution and mechanical properties of extruded Mg-4.58Zn-2.6Gd-0.18Zr alloy were investigated at extrusion temperatures of 260 °C, 280 °C and 300 °C, extrusion ratios of 10, 15 and 30, and ram speeds of 3 mm s−1 and 6 mm s−1, respectively. The results indicated that the as-cast experimental alloy was composed of α-Mg matrix, coarse α-Mg + W(Mg3Zn3Gd2) eutectic and icosahedral quasicrystalline I(Mg3Zn6Gd) phase. A small amount of undissolved W phases were detected after the homogenization treatment at 505 °C up to 16 h, while most I phase dissolved into the α-Mg matrix. The initial crystallites before extrusion were randomly oriented, and showed a typical random texture. After extrusions, all samples exhibited a bimodal microstructure consisting of fine Dynamic recrystallization (DRX) grains and coarse elongated un-DRX grains, and the formation of ultra-fine DRX grains only occurred in the sample with an extrusion ratio of 10 at 260 °C, 3 mm s−1, which was caused by the solute segregation in homogenized billets and non-uniformly distributed W phase during the extrusion process. A fiber texture with {0002} planes and <1̄21̄0> directions paralleled to the extrusion direction was observed to be dominant in all the extruded samples. Furthermore, the increase of extrusion ratio was found to be beneficial for the DRX process and refinement of grain size, and the maximum texture intensity was accordingly weakened, which resulted in a decrease of tensile yield strength but an increase of elongation. With increasing the extrusion temperature or ram speed, both the grain size and DRX fraction gradually increased. Consequently, the texture was randomized and the maximum texture intensity decreased, which led to a reduction of the elongation and tensile yield strength. The tensile failure behaviors under different extrusion conditions were found to be related with the contraction twin lamellas formed in the un-DRX grains and the string-like W phases.

Unveiling Mechanical Response and Deformation Mechanism of Extruded WE43 Mg Alloy under High-Speed Impact

Superplastic Deformation Mechanisms of Coarse-Grained Rolled Mg-4Y-3RE Magnesium Alloy

Plastic deformation behaviors and microstructures of a wrought Mg-Zn-rare earth alloy

The Deformation Mechanism and Adiabatic Shearing Behavior of Extruded Mg-8.0Al-0.1Mn Alloy in Different Heat Treated States under High-Speed Impact Load

Unveiling the mechanical response and deformation mechanism of extruded Mg-2.5Nd-0.5Zn-0.5Zr alloy sheet under high-temperature tensile

Effects of temperature and strain rate on deformation behaviors of an extruded Mg-5Zn-2.5Y-1Ce-0.5Mn alloy

The microstructure evolution and deformation mechanism in a casting AM80 magnesium alloy under ultra-high strain rate loading

Deformation behaviors and the related high-temperature mechanical properties of Mg-11Gd-5Y-2Zn-0.7Zr via regulating extrusion temperatures

Microstructure Evolution and Deformation Behavior of Extruded Mg-5Al-0.6Sc Alloy during Room and Elevated Temperature Tension Revealed by Ex-Situ EBSD and VPSC

Unveiling the mechanical response and accommodation mechanism of pre-rolled AZ31 magnesium alloy under high-speed impact loading

Effect of extrusion temperature on microstructure, mechanical properties, and deformation mechanism of Mg-2.5Er-0.6Zr alloy

High-Speed Impact Behavior and Microstructure Evolution of an Extruded Mg-7Sn-5Zn-3Al Alloy

In-Situ Analysis of the Tensile Deformation Modes and Anisotropy of Extruded Mg-10gd-3y-0.5zr (wt.%) at Elevated Temperatures

High Temperature Compressive Deformation Behavior of an Extruded Mg–8Gd–3Y–0.5Zr (wt.%) Alloy

Dynamic tensile properties and microstructural evolution of extruded EW75 magnesium alloy at high strain rates

Dynamic recrystallization mechanism and near-isotropic mechanical properties of WE43 magnesium alloy sheets rolled at different temperatures

Hot deformation behaviors of an extruded Mg-Li-Zn-Ce-Y-Zr alloy

Hot Deformation and Dynamic Recrystallization Behaviors of Mg–Gd–Y–Zr Alloy

Comparative Study of Hot Deformation Behavior and Microstructure Evolution of As-Cast and Extruded WE43 Magnesium Alloy

Effects of the Extrusion Parameters on Microstructure, Texture and Room Temperature Mechanical Properties of Extruded Mg–2.49Nd–1.82Gd–0.2Zn–0.2Zr Alloy

Microstructure, Texture Evolution and Tensile Properties of Extruded Mg-4.58Zn-2.6Gd-0.16Zr Alloy