Microstructural Characterization of Stellite 6 Alloy Processed by Electron Beam Melting

Bin Chen,Rui Chen,Yun Fan,Zhiqing Chen,Zhixian Zhao

DOI: https://doi.org/10.1016/j.vacuum.2024.113591

IF: 4

2024-01-01

Vacuum

Abstract:Stellite 6 alloy was subjected to electron beam melting (EBM) processing in this study. The main phases in the alloy are alpha-Co, epsilon-Co, M23C6 (M = Cr, Co, W, etc.), and M7C3 (M = Cr, Co, W, etc.) carbides. The microstructure of the EBM-processed Stellite 6 alloy comprises grains of relatively uniform sizes, with an average grain size of 11.1 mu m. There is a relatively minor internal strain within the alloy. The majority of grains exhibit low intragranular misorientations, approximately around 0.5 degrees, while a minority of grains display relatively larger intragranular misorientations, around 2.8 degrees. The dominant {100} texture was developed in the build direction because of the fast growth of the <100> direction for a cubic crystal structure during solidification. The vertically aligned columnar grains contribute to the development of the <100> texture along the build direction. The elongated direction of columnar grains was parallel to the temperature gradient direction. This competitive growth direction at the solid-liquid interface results in slight tilts in the pole figures. The eutectic carbide phases are uniformly distributed along the grain boundaries. The cube-cube orientation relationships between the matrix and M23C6 carbide phase were identified as [001](alpha)//[111]M23C6. The low stacking fault energy of the Stellite 6 alloy resulted in the formation of a high density of stacking faults within the grains. The interactions between stacking faults of different orientations were observed. Primary M7C3 carbides were found to transform into secondary M23C6 carbides, with a phase transition process observed where secondary carbides M23C6 surrounded primary carbides M7C3.