Abstract:To enhance the low-temperature plasticity and high-temperature strength of molybdenum alloys, we introduce a method of uniformly dispersing nano-ZrTiO4 particles within and between molybdenum grains. This approach effectively eliminates the formation of hard agglomerations between particles and leads to a further refinement of molybdenum grains. The research employs molecular level solid-liquid doping and subsequent liquid dispersion evaporation techniques to successfully synthesize Mo-ZrTiO4 nano-composite powder following H2 reduction. Subsequently, a novel fine-grained Mo-ZrTiO4 alloy sintered billet is successfully fabricated through cold isostatic pressing and high-temperature sintering. To assess the efficacy of the process, three sets of comparative experiments are designed, each employing different methods. The comparative studies have revealed compelling advantages of the liquid dispersed evaporated fine-grained samples of Mo-ZrTiO4. The key advantages identified are as follows:the samples demonstrate a refined grain size, ranging from 2 mu m to 4 mu m. Within the samples, the nano ZrTiO4 particles have an average size of approximately 200 nm. The density and Vickers hardness of the samples is measured at 10.21 g/cm3 and 268.5 +/- 17HV0.2, respectively. The samples exhibit impressive toughness even at room temperature, notably, the high-temperature compressive strength of these samples surpasses that of the deformed samples reported in previous literature concerning this system. The mechanism of liquid dispersion evaporation method in grain nucleation, growth, and powder drying, reduction, and sintering processes was systematically elaborated. Simultaneously, a detailed analysis was conducted on two high-temperature strengthening mechanisms that impact the mechanical properties. The results indicate that this excellent performance can be attributed to the synergistic effect of both fine grain strengthening and uniform dispersion strengthening of second-phase nanoparticles.

The Effect of In-Situ ZrO2 on Compressive Properties of Molybdenum-Rhenium Alloys and Strengthening Mechanism

Effects of Mo and Zr Composite Additions on the Microstructure, Mechanical Properties and Oxidation Resistance of Multi-Elemental Nb-Si Based Ultrahigh Temperature Alloys

Microstructure and High Temperature Deformation Behavior of the Mo-ZrO 2 Alloys

Excellent High-Temperature Strength and Ductility of the ZrC Nanoparticles Dispersed Molybdenum

Evaluating compressive property and hot deformation behavior of molybdenum alloy reinforced by nanoscale zirconia particles

Evaluation of tensile property and strengthening mechanism of Zirconia reinforced molybdenum alloy

The Effects of Refractory Elements on Mechanical Properties in CoCrNiFe Concentrated Solid Solution Alloys Across Different Temperatures

Compositional Effect on Microstructure and Mechanical Properties of AlNbTiZr-based Refractory High Entropy Alloys

Effect of rare earth oxide doping on microstructure and mechanical property of Mo-30 W solid solution alloy

Mechanical and microstructural responses in molybdenum-rhenium alloys under hot compressions

Study on preparation and properties of molybdenum alloys reinforced by nano-sized ZrO 2 particles

Effect of Zr on property and microstructure of Mo-Zr alloy

Microstructural evolutions of molybdenum‐rhenium (47.5 wt.%) alloy under room and high temperature compressions

Evaluating low cycle fatigue property of nanoscale ZrO2 particles strengthening molybdenum alloy

Mechanical properties and corrosion behavior in molten zinc of Mo–ZrO 2 alloys

Microstructure and high-temperature deformation performance of liquid-dispersed evaporated Nano-ZrTiO4 doping molybdenum alloy

Effects of Minor Zr Addition on the Microstructure and Mechanical Properties of Laser Welded Dissimilar Joint of Titanium and Molybdenum

Enhanced Mechanical Properties of Molybdenum Alloy Originating from Composite Strengthening of Re and CeO2

Effect of zirconia on low cycle fatigue and energy absorption of molybdenum alloy

Preparation,performance and Structure of High Tenacious Mo-0.1Zr Alloy

Tensile behavior and microstructure evolution of Mo-14 %Re alloy at room temperature and elevated temperatures