Abstract:Titanium alloy is a major structural material with excellent high specific strength in aerospace applications. Cubic boron nitride (cBN) is a synthetic wear-resistant material with high hardness, similar to that of diamond, that is used in mechanical cutting and grinding. In addition, the thermal stability of cubic boron nitride particles is much better than that of diamond. In order to further enhance the wear resistance of the Ti6Al4V alloy, the laser cladding (LC) technology characteristics of metallurgical bonding were used to prepare cubic boron nitride/Ti6Al4V and Ni-plated cubic boron nitride/Ti6Al4V composite coatings on Ti6Al4V substrates in this paper. However, in the laser molten pool, it is difficult to retain the raw properties of cubic boron nitride particles under laser radiation. Both composite coatings were analyzed using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). The microstructures and interface bonding between cubic boron nitride particles and the Ti6Al4V matrix were examined using SEM, and the wear resistance and the worn track morphology of the composite coatings were evaluated using the ball-on-disc wear test and step profiler (WTM-2E). The results indicated that the Ni-plated cubic boron nitride/Ti6Al4V composite coating showed fewer thermal defects in comparison with the cubic boron nitride/Ti6Al4V coating. The Ni plating on the surface of cubic boron nitride particles was able to avoid the generation of thermal cracking of the cubic boron nitride particles in the composite coating. The TiN reaction layer was formed between the cubic boron nitride particles and Ti6Al4V matrix, which effectively prevented the further decomposition of the cubic boron nitride particles. The XRD and XPS results confirmed that the TiN reaction layer formed between the cubic boron nitride particles and Ti6Al4V. The Ni plating on the surface of the cubic boron nitride particles was also beneficial for increasing the wear resistance of the composite coating.

Microstructure and Performance of (Cocrni)88al6ti6-Cbn Composite Coatings by High-Speed Laser Cladding (HSLC): A Novel Strategy for Synergizing Wear-Resistance and Friction Reduction

Microstructure and performance of (CoCrNi) 88 Al 6 Ti 6 -cBN composite coatings by high-speed laser cladding (HSLC): A novel strategy for synergizing wear-resistance and friction reduction

Microstructure and tribological properties of laser cladded self-lubricating nickel-base composite coatings containing nano-Cu and h-BN solid lubricants

Effect of c-BN on the microstructure and high temperature wear resistance of laser cladded Ni-based composite coating

Development and Characterization of Laser Clad High Temperature Self-Lubricating Wear Resistant Composite Coatings on Ti–6Al–4V Alloy

Study on the Wear and Corrosion Resistance of CoCrFeNiTi0.8-xcBN Laser Cladding Coatings

Wear Behaviors of TiN/WS2 + hBN/NiCrBSi Self-Lubricating Composite Coatings on TC4 Alloy by Laser Cladding

Microstructure and tribological behaviors of laser cladded CuAlMnTi–xTiC composite coatings at elevated temperature

Tribological Performance and Wear Mechanism of Laser Cladded NiCrAl-WC Coatings at High-Temperature

Effect of SiC and TiC content on microstructure and wear behavior of Ni-based composite coating manufactured by laser cladding on Ti-6Al-4V

Comparison of the Microstructure Evolution and Wear Resistance of Ti6Al4V Composite Coatings Reinforced by Hard Pure or Ni-plated Cubic Boron Nitride Particles Prepared with Laser Cladding on a Ti6Al4V Substrate

Microstructure and tribological performance of Ni60-based composite coatings on Ti6Al4V alloy with different Ti3SiC2 ceramic additions by laser cladding

Microstructure and Tribological Properities of Laser Clad Zr-Al-Ni-Cu Composite Coating

Improved Wear Resistance of TiAl Composite Coatings Through NbC@(Ti,Nb)2AlC Core-Shell Structure and Nanoscale Precipitation Strengthening

High Temperature Wear Performance of In-Situ Forming Textured Ni60/WC/h-BN Composite Coatings Based on Laser Micro-Cladding

Microstructure of Laser-Clad High-Temperature Self-Lubricating Wear-Resistant Composite Coatings

Improved wear resistance of TiAl composite coatings through NbC@(Ti,Nb) 2 AlC core-shell structure and nanoscale precipitation strengthening

Beneficial effects of Co to CoCrNiMoCB coatings obtained by laser cladding

Microstructure and Wear Resistance of Laser Cladding nano TiC/micro TiB2/C-276 Composite Coatings on 316L Stainless Steel

High-temperature oxidation and wear properties of TiC-reinforced CrMnFeCoNi high entropy alloy composite coatings produced by laser cladding

Study on fabrication of multi-phase reinforcement coatings on Ti6Al4V by laser cladding for enhanced tribological performance