Abstract:A comparative experimental and numerical study of the impact behaviour of carbon-fiber-reinforced thermoplastic (TP) and thermoset (TS) composites has been carried out. On the one hand, low velocity impact (LVI) tests were performed on TP and TS composites with different lay-up sequences at different energy levels, and the damage modes and microscopic damage mechanisms after impact were investigated using macroscale inspection, C-scan inspection, and X-ray-computed tomography. The comparative results show that the initial damage valve force under LVI depends not only on the material, but also on the layup sequence. The initial valve force of the P2 soft layer with lower stiffness is about 11% lower than that of the P1 quasi-isotropic layer under the same material, while the initial valve force of thermoplastic composites is about 28% lower than that of thermoset composites under the same stacking order. Under the same stacking order and impact energy level, the damage area and depth of TP composites are smaller than those of TS composites; while under the same material and impact energy level, the indentation depth of P2 plies is greater than that of P1 plies, and the damage area of P2 plies is smaller than that of P1 plies, but the change of thermoplastic composites is not as obvious as that of thermoset composites. This indicates that TP composites have a higher initial damage threshold energy and impact resistance at the same lay-up order, while increasing the lay-up ratio of the same material by 45° improves the impact resistance of the structure. In addition, a damage model based on continuum damage mechanics (CDM) was developed to predict different damage modes of thermoplastic composites during low velocity impact, and the analytical results were compared with the experimental results. At an impact energy of 4.45 J/mm, the error of the initial damage valve force is 5.26% and the error of the maximum impact force is 4.36%. The simulated impact energy and impact velocity curves agree with the experimental results, indicating that the finite element model has good reliability.

Prediction of Low-Velocity Impact Mechanical Response and Damage in Thermoplastic Composites Considering Elastoplastic Behavior

Finite Element Analysis of a Modified Progressive Damage Model for Composite Laminates under Low-Velocity Impact

A Progressive Damage Model of Composite Laminates under Low-Velocity Impact

Numerical Investigation on the Repeated Low-Velocity Impact Behavior of Composite Laminates

Exploration of Several Influence Factors of Low-Velocity Impact Damage on Composite Laminates

Experimental and Simulation Study on Failure of Thermoplastic Carbon Fiber Composite Laminates under Low-Velocity Impact

Low-velocity impact behavior and residual tensile strength of CFRP laminates

Prediction of low‐velocity impact dent for composite laminates based on an anisotropic elastoplastic damage model

A 3D objective material model for elastic-plastic damage behavior of fiber reinforced polymer composites

A Novel Integrated Modeling Strategy for Predicting Damage Mechanisms and Energy Dissipation of Composite Stiffened Structures under Low-Velocity Impact and Compression

A Dynamic Constitutive Model for Fiber-Reinforced Composite under Impact Loading

Predicting Damage Behaviors of Composite Laminates under Multiple Low‐velocity Impacts

Prediction of Load-Bearing Capacity of Composite Parts with Low-Velocity Impact Damage: Identification of Intra- and Inter-Ply Constitutive Models

Finite Element Method of a Progressive Intralaminar and Interlaminar Damage Model for Woven Fibre Laminated Composites under Low Velocity Impact

An enhanced elastoplastic damage coupled model for compression characteristics analysis of continuous fiber-reinforced thermoplastic composite stiffened panel

An evaluation of progressive damage analysis methods for modeling low velocity impact of thermoplastic composites

Impact Behavior Analysis of Carbon Fiber Reinforced Aluminum Laminates Based on a Micro-Mechanical Damage Model

Study on the Low-Velocity Impact Response and Damage Mechanisms of Thermoplastic Composites

Assessment of Failure Criteria and Damage Evolution Methods for Composite Laminates under Low-Velocity Impact

Development and experimental verification of an advanced 3D elastoplastic progressive damage model for composite materials

Finite element analysis of dynamic progressive failure of carbon fiber composite laminates under low velocity impact