Abstract:Abstract The Yb:Lu 2 O 3 precursor made up of spherical particles was synthesized through the co-precipitation method in the water/ethanol solvent. The 5 at% Yb:Lu 2 O 3 powder is in the cubic phase after calcination at 1100 °C for 4 h. The powder also consists of spherical nanoparticles with the average particle and grain sizes of 96 and 49 nm, respectively. The average grain size of the pre-sintered ceramic sample is 526 nm and that of the sample by hot isostatic pressing grows to 612 nm. The 1.0 mm-thick sample has an in-line transmittance of 81.6% (theoretical value of 82.2%) at 1100 nm. The largest absorption cross-section at 976 nm is 0.96×10 −20 cm 2 with the emission cross-section at 1033 nm of 0.92×10 −20 cm 2 and the gain cross sections are calculated with the smallest population inversion parameter β of 0.059. The highest slope efficiency of 68.7% with the optical efficiency of 65.1% is obtained at 1033.3 nm in quasi-continuous wave (QCW) pumping. In the case of continuous wave (CW) pumping, the highest slope efficiency is 61.0% with the optical efficiency of 54.1%. The obtained laser performance indicates that Yb:Lu 2 O 3 ceramics have excellent resistance to thermal load stresses, which shows great potential in high-power solid-state laser applications.

Optical Properties and Laser Performance of Ho : LuAG Ceramics

Optical Properties And Laser Performance Of Ho:Luag Ceramics

Optical Properties Of Ho: Yag And Ho: Luag Polycrystalline Transparent Ceramics

Fabrication and Properties of High Quality Transparent Ho:YAG Ceramics

Effect of Agglomeration State of Starting Powder on Fabrication of Tm,Ho Co-Doped LuAG Transparent Ceramics

Polycrystalline Ho:YAG transparent ceramics for eye-safe solid state laser applications

Laser grade Yb:LuAG transparent ceramic prepared by nanocrystalline pressure-less sintering in reducing H_2

Yb:LuAG Laser Ceramics: a Promising High Power Laser Gain Medium

Fabrication and luminescent properties of holmium doped Y2Zr2O7 transparent ceramics as new type laser material

Fabrication, Optical Properties and LD-pumped 2.7 Μm Laser Performance of Low Er3+ Concentration Doped Lu2O3 Transparent Ceramics

Fabrication and Optical Properties of Ce, Pr Co-doped LuAG Transparent Ceramics

Fabrication, microstructure and optical characterizations of holmium oxide (Ho2O3) transparent ceramics

Continuous-wave and Q-switched operation of a resonantly pumped polycrystalline ceramic Ho:LuAG laser.

2.1 Μm Ho:LuAG Ceramic Laser Intracavity Pumped by a Diode-Pumped Tm:YAG Laser

Fabrication And Spectroscopic Properties Of Nd:Lu2o3 Transparent Ceramics For Laser Media

Effects of Ho3+-Doping Concentration on the Performances of Resonantly Pumped Ho:Yag Ceramic Lasers

Fabrication and characterization of LuAG: Er ceramics with high optical transmission

Fabrication, microstructures, and optical properties of Yb:Lu2O3 laser ceramics from co-precipitated nano-powders

High luminous efficiency and high saturation threshold in highly transparent LuAG:Ce phosphor ceramics for laser diodes lighting

Fabrication, microstructure and optical properties of Yb:LuxY3-xAl5O12 transparent ceramics

Growth, Thermal, and Optical Properties of a Novel Mid-Infrared Ho:LuYAP Laser Crystal