Performance Enhancement of Cement Mortar with Superabsorbent Polymer Composite Internally Embedded with Porous Ceramsite Sand

Jin Yang,Yongpeng Liu,Jingyi Zeng,Ying Su,Fulong Wang,Xingyang He

DOI: https://doi.org/10.1016/j.jobe.2024.110532

IF: 7.144

2024-01-01

Journal of Building Engineering

Abstract:Superabsorbent polymer (SAP), which can act as water reservoir, was an internal curing (IC) agent with great potential to reduce the shrinkage and cracking of cement-based materials. However, the volume shrinkage of SAP after water release will lead to the formation of additional voids, which will lead to a clear reduction of mechanical properties. In present work, a novel SAP composite with a rigid skeleton (IP-PS) was synthesized by embedding in-situ polymerized SAP hydrogel into the pores of porous ceramic (PS). The results demonstrated that the compressive strength of IP-PS0.054 was above 10% higher than that of SAP0.054 in the early and late stages, the compressive strength of IP-PS0.054 at 28 days reached 97.71% of that of the control group, which was predominantly ascribed to the support provided by the embedded skeleton. The development of self-desiccation was also notably delayed by the incorporation of IP-PS, as evidenced by the approximately 12% reduction compared to SAP0.054 and 47% reduction compared to Control group in 7-day autogenous shrinkage, which was on account of the enhanced water storage and durable IC capacity of IP-PS. Furthermore, the impermeability of cement-based materials was also improved by the in-situ polymerized hydrogel modification.