Abstract:A thermosetting resin system has been developed by the copolymerization of allyl phenoxy, bismaleimide (BMI), and diallyl bisphenol A and optimized using response surface methodology. An optimized modified resin system with enhanced properties was achieved based on empirical second-order models expressing the relationship between the modifier contents and the mechanical properties. Dicumyl peroxide (DCP) was selected as initiator to further improve the curing behavior and mechanical properties of the optimized resin system. The effect of initiator contents on impact, flexural strength, and heat distortion temperature was also investigated. The curing behavior, morphology, and thermal stability of the optimized resin were carefully characterized using differential scanning calorimeter, scanning electron microscope, and thermogravimetric and dynamic mechanical analyzers, respectively. For evaluating the efficiency of modified BMI resin system, laminated composites using glass fiber cloth were fabricated using a hot press and tested for mechanical properties. The results showed that the DCP reduced the curing temperature significantly, improved the curing process, and proved to be very effective in heat resistance. Meanwhile, the laminated composite with initiator showed 13–27% higher mechanical properties and 5–7% higher retention rate at high temperature when compared with the neat resin composite system. The optimized resin system with higher mechanical properties, good heat resistance, and better manufacturability can be used as matrix resin for making advanced fiber-reinforced composites.

Fluorinated Polyetherimide As the Modifier for Synergistically Enhancing the Mechanical, Thermal and Dielectric Properties of Bismaleimide Resin and Its Composites

Morphology and mechanical properties of poly(ether-imide)-modified polycyanurates

Synthesis of a Novel Hyperbranched Polyimide for Reinforcing Toughness and Insulating Properties of Bismaleimide Resin

POLYESTERIMIDE-MODIFIED BISMALEIMIDE RESINS. I. EFFECT OF POLYESTERIMI DE CONTENT

Bismaleimide-modified methyl-di(phenylethynyl)silane blends and composites: Cure characteristics, thermal stability, and mechanical property

Polyetherimide-modified bismaleimide resins. II. Effect of polyetherimide content

Eugenol‐Derived Bismaleimide High Performance Resins and Composites Using Diisocyanate As Property Modifier

Phosphorus-containing Flame-Retardant Bismaleimide Resin with High Mechanical Properties

Fluorinated Bismaleimide Resin with Good Processability, High Toughness, and Outstanding Dielectric Properties

Preparation and properties of BMI resin modified by fluorene-containing poly(arylene ether ketone)

Studies of modified bismaleimide resins Part I The influence of resin composition on thermal and impact properties

Influence of Composition on the Properties of BMI Neat Resins and BMI/T300 Composites

Fabricating advanced MXene-based hybrid materials to elevate fire safety and mechanical strength in carbon fiber-reinforced bismaleimide resins

Mechanical and thermal properties of synergistic modification of bismaleimide polymer composites with nano‐SiO2 and hyperbranched polyimide

Polyhedral oligosilsesquioxane-modified boron nitride enhances the mechanical properties of polyimide nanocomposites

High toughness and excellent electrical performance bismaleimide resin modified by hyperbranched unsaturated polyester of flexible aliphatic side chains

Effect of Polyether Sulfone Resin on Micromorphology, Thermal, Mechanical, and Dielectric Properties of Epoxy–Bismaleimide Composite Material

Enhanced toughness and thermal properties of bismaleimide resin based on the synergistic effect of reactive amino‐terminal poly(phthalazinone ether nitrile sulfone) and bisallyl bearing diphenol group

Preparation and Characterization of Bismaleimide-Resin-Based Composite Materials

Enhancement of Thermal and Mechanical Properties of Bismaleimide Using a Graphene Oxide Modified by Epoxy Silane

Optimization and preparation of an allyl phenoxy-modified bismaleimide resin