Abstract:The practical application of high-voltage lithium cobalt oxide (LCO) has been hampered by the severe degradation of its structural integrity. In this work, a protective bilayer was fabricated on LCO surfaces by means of large-scale and facile electrolyte engineering. The protective bilayer consisting of a LiF-rich cathode-electrolyte interphase (CEI) as the outermost layer and a layer of disordered spinel structure as the inner layer was uniformly fabricated in-situ. The high-resistance CEI layer inhibited the fast transfer of Li ions from LCO to bulk electrolyte during the first few cycles, resulting in the significantly increased local overpotential on the LCO surface. As a consequence, the LCO surface underwent a phase transformation from the layered phase to the spinel phase first, forming the spinel phase inner layer due to the voltage rising beyond 4.55 V (vs. Li/Li + ). The CEI and spinel layers effectively blocked the dissolution of transition-metal (TM) ions into the electrolyte during cycling and inhibited the formation of the structurally defective rock-salt phase that would hasten cycling-induced structural degradation. The formation of the protective bilayer effectively prevented the phase transition from the bulk layered LCO structure into spinel and then rock salt, thereby reducing decay of its cycling capacity. Remarkably, the graphite||LCO pouch cell with optimized electrolyte retained 78.9% of its capacity even after 1000 cycles under the operation voltage window of 3.0-4.55 V (vs. Li/Li + ). This study provides guidance for the development of effective surface treatment strategies for stable layered cathodes with high capacity and cyclability.

Multifunctional Surface-Integrated Structures Enabling Layered Oxide Cathodes with Stable High-Voltage Cycling

Realizing Superior Cycling Stability of Ni-Rich Layered Cathode by Combination of Grain Boundary Engineering and Surface Coating

Surface Phase Engineering Stabilizes Cycling of Zero-Cobalt Single-Crystalline Layered Cathodes

Single-crystal Li-rich Layered Cathodes with Suppressed Voltage Decay by Double-Layer Interface Engineering

Regulating Surface and Grain-Boundary Structures of Ni-Rich Layered Cathodes for Ultrahigh Cycle Stability

Surface-interspersed nanoparticles induced cathode-electrolyte interphase enabling stable cycling of high-voltage LiCoO 2

Mitigating Voltage Decay of Li-Rich Layer Oxide Cathode Material Via an Ultrathin “lithium Ion Pump” Heteroepitaxial Surface Modification

Surface-interspersed Nanoparticles Induced Cathode-Electrolyte Interphase Enabling Stable Cycling of High-Voltage LiCoO2

Enabling Superior Electrochemical Performance of Lithium-Rich Li1.2Ni0.2Mn0.6O2 Cathode Materials by Surface Integration

Stable Cycling of LiNi0.9Co0.05Mn0.05O2/lithium Metal Batteries Enabled by Synergistic Tuning the Surface Stability of Cathode/anode

In-Situ Constructed Protective Bilayer Enabling Stable Cycling of LiCoO 2 Cathode at High-Voltage

In-situ Constructed Protective Bilayer Enabling Stable Cycling of LiCoO2 Cathode at High-Voltage

Constructing Stable Interface Layer for Boosting High-Voltage Cycling Performance of Single-Crystal Ni-rich Cathodes

Structural self-reconstruction strategy empowering Ni-rich layered cathodes with low-strain for superior cyclabilities

Enhancement on the Cycling Stability of the Layered Ni-Rich Oxide Cathode by In-Situ Fabricating Nano-Thickness Cation-Mixing Layers

Optimizing Both Bulk and Surface Structure of Li‐Rich Layered Cathodes for Long‐Life and Safe Li‐Ion Batteries

<i>In</i><i>-situ</i> constructed protective bilayer enabling stable cycling of LiCoO<sub>2</sub> cathode at high-voltage

Enhancing the Stability of Li-Rich Mn-Based Oxide Cathodes Through Surface High-Entropy Strategy

In-situ Surface Modification to Stabilize Ni-rich Layered Oxide Cathode with Functional Electrolyte

Controllable oxygen vacancies (in surface and bulk) to suppress the voltage decay of Li-rich layered cathode

Stabilizing Li-rich Layered Cathode Materials by Nanolayer-Confined Crystal Growth for Li-ion Batteries