Directional coarsening behavior of primary γ′ phase in Ni3Al-based superalloy during aging heat treatment
Xin He,Chang Liu,Yikai Yang,Jian Ding,Xueguang Chen,Xingchuan Xia,Ying Tang,Yongchang Liu
DOI: https://doi.org/10.1016/j.jallcom.2021.159674
IF: 6.2
2021-08-01
Journal of Alloys and Compounds
Abstract:<p>Polycrystalline Ni<sub>3</sub>Al-based superalloy with up to 70% <span class="math"><math>γ′</math></span> phase owns excellent strength at around 1100 °C. It has been successfully used as a substitute for turbine blade crown, which is one of the aircraft components working in the severest environment (i.e., sometimes nearly overheating). However, few studies concentrate on the coarsening resistance and phase thermal stability in this newly designed polycrystalline superalloy at the working temperature, hence, directional coarsening behavior of primary <span class="math"><math>γ′</math></span> <span class="math"><math>(γI′)</math></span> has remained restricted. This paper investigated directional coarsening behavior of <span class="math"><math>γI′</math></span> during aging treatment (1100 °C) after overheating at 1270 °C with furnace cooling (SFA), air cooling (SAA) and water cooling (SWA) respectively. It clearly showed that <span class="math"><math>γI′</math></span> grew into lamellar and gradually became irregular during the directional coarsening process. Moreover, its morphological combination mode was illustrated. Since parallel short lamellar <span class="math"><math>γI′</math></span> connected each other, long lamellar formed. When perpendicular long lamellar <span class="math"><math>γI′</math></span> connected each other, it became <span class="small-caps">L</span>-type or T-type, i.e., precursor of irregular <span class="math"><math>γI′</math></span>. The kinetics of directional coarsening regime of <span class="math"><math>γI′</math></span> was in line with the matrix-diffusion<sub>-</sub>controlled (MDC) theory according to the evaluation of <span class="math"><math>γI′</math></span> size. This was caused by higher migration of <span class="math"><math>γI′</math></span> interfaces than the diffusion of solute elements. It was also confirmed that driving force of directional coarsening mainly depended on the competition of elemental diffusion, lattice misfit distribution and <span class="math"><math>γ</math></span> channel distance.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering