Flow-Induced Crystallization Coupled with Strong Memory Effect: Revealing Melt Heterogeneity

Ruijun Zhao,Yingzhuo Liu,Xinyu Liu,Yuanqiao Gao,Zhe Ma

DOI: https://doi.org/10.1021/acs.macromol.4c01252

IF: 5.5

2024-01-01

Macromolecules

Abstract:Herein, the flow-induced crystallization coupled with an intrinsic strong memory effect was investigated via in situ wide-angle X-ray diffraction. A poly(butene-1) random copolymer with 4.3 mol % ethylene co-units was utilized as the model polymorphic material to examine memory effect induced by crystallization kinetics and polymorphism. The quiescent crystallization results clearly demonstrated that the melt-memory effect was able to induce a heterogeneous melt even above the equilibrium melting temperature, in which locally segregated segments comprised the residual domains and effectively facilitated the formation of the most stable phase (trigonal form I ') rather than the kinetically favored phase (tetragonal form II). Form I ' exhibited more pronounced accelerated crystallization kinetics than form II as the melt temperature (T-melt) was decreased, enhancing melt heterogeneity, and became the kinetically favored phase at T-melt = 120 degrees C. Subsequently, the complex mutual effect of flow was explored in the heterogeneous melt, in which crystallization exhibited a dependence on flow strength. For mild flow at 0.3 s(-1), flow mainly accelerated the crystallization of oriented form II while that of form I ' was hardly affected, in contrast to the melt-memory effect observed during the aforementioned quiescent crystallization. The distinct responses to macroscopic flow revealed not only the dependence of tetragonal and trigonal phase formation but also the heterogeneous melt response.