Effects of strain rate and temperature on polymorphism in flow-induced crystallization of Poly(vinylidene fluoride)

Zhaozhe Chu,Long Liu,Yilong Liao,Wei Li,Ruijun Zhao,Zhe Ma,Yuesheng Li

DOI: https://doi.org/10.1016/j.polymer.2020.122773

IF: 4.6

2020-08-01

Polymer

Abstract:<p>The flow-induced crystallization of poly(vinylidene fluoride) (PVDF) was investigated over the broad strain rate and temperature ranges by combining the in situ synchrotron small- and wide -angle X-ray scattering with the extensional rheometer. The results show that temperature and strain rate collectively affect the crystallization polymorphism of PVDF. At 155–170 °C, the electroactive β-phase was generated during flow (strain = 2.7 and strain rate = 10 s⁻¹), without the appearance of customary kinetically favorable α-phase. For the same flow at a higher temperature of 180 °C, the fibrillar shish were formed but did not develop into crystallites yet. During the followed post-flow isothermal process at 155 °C, those flow-generated β-phase grew pronouncedly and γ-phase unexpectedly appeared at just 5 min. Differently, pure β-phase existed at 160–170 °C, while no crystallites were detected at 180 °C. On the other hand, for the flow of strain 2.7, the broad strain rate range of 0.01–10 s⁻¹ could induce the formation of pure β-phase during flow and the subsequent isothermal periods at 160 °C. When the partially crystallized PVDF was cooled down, α-phase was triggered by the increased undercooling. Interestingly, although the aforementioned variation of flow conditions significantly changes the formation of β-phase, the corresponding appearance temperature of α-phase remains at a comparable temperature of around 149 °C, which is even similar with that of quiescent crystallization.</p>

polymer science