Abstract:Low carbon ferrochrome slag (LCFS) is the metallurgical waste slag from the carbon ferrochrome alloy smelting process. Compared with high carbon ferrochrome slag, LCFS has great potential as cementitious material; the chemical compositions of the two types of slag are quite different. In this research, composite cementitious materials are prepared which use low carbon ferrochrome slag and granulated blast furnace slag (GBFS) as the main raw material. Steel slag mud (SSM) and flue gas desulfurization gypsum (FGDG) are used as the activator. In order to find the variety rule of compressive strength on the composite cementitious materials, a three-factor three-level Box-Behnken design is used to discuss the following independent variables: LCFS content, GBFS content, and water-binder ratio. Moreover, the hydration characteristics of the LCFS-GBFS composite cementitious materials is studied in this paper in terms of hydration product, micromorphology, and hydration degree, based on multi-technical microstructural characterizations. The results show that the compressive strength of the LCFS-GBFS composite cementitious materials is significantly affected by single factors and the interaction of two factors. The mechanical property of the mortar samples at 3, 7, and 28 days are 26.6, 35.3, and 42.7 MPa, respectively, when the LCFS-GBFS-SSM-FGDG ratio is 3:5:1:1 and the water-binder ratio is 0.3. The hydration products of LCFS-GBFS composite cementitious materials are mainly amorphous gels (C-S-H gel), ettringite, and Ca(OH)2. With the increase of LCFS content, more hydration products are generated, and the microstructure of the cementitious system becomes more compact, which contributes to the compressive strength. The results of this research can provide a preliminary theoretical foundation for the development of LCFS-GBFS composite cementitious materials and promote the feasibility of its application in the construction industry. Deep hydration mechanism analysis and engineering applications should be studied in the future.

Mechanical Properties, Microstructure and Life-Cycle Assessment of Eco-Friendly Cementitious Materials Containing Circulating Fluidized Bed Fly Ash and Ground Granulated Blast Furnace Slag

The Impact of Fly Ash on the Properties of Cementitious Materials Based on Slag-Steel Slag-Gypsum Solid Waste

Utilization of coal gangue power generation industry by-product CFA in cement: Workability, rheological behavior and microstructure of blended cement paste

Development of gastrin synthesis and posttranslational processing mechanisms in rats.

Investigating the Hydration, Mechanical Properties, and Pozzolanic Activity of Cement Paste Containing Co-Combustion Fly Ash

Utilization of Corn Cob Ash as Fine Aggregate and Ground Granulated Blast Furnace Slag as Cementitious Material in Concrete

Compressive Strength and Microstructural Development of Cementitious Mixtures Incorporating Ultrafine Granulated Blast Furnace Slag

Resource utilization of solid waste from steel industries in cement-based cementitious materials: Mechanical properties, hydration behaviors, and environmental impact

Preparation and Hydration Mechanisms of Low Carbon Ferrochrome Slag-Granulated Blast Furnace Slag Composite Cementitious Materials

Hydration and microstructure evolution of a novel low-carbon concrete containing recycled clay brick powder and ground granulated blast furnace slag

Performance of Green Binder Developed from Flue Gas Desulfurization Gypsum Incorporating Portland Cement and Large-Volume Fly Ash

Optimization design and mechanical properties of multi-component ecological gelling materials

Preparation and curing method of red mud-calcium carbide slag synergistically activated fly ash-ground granulated blast furnace slag based eco-friendly geopolymer

Enhancement of compressive strength of high-volume fly ash cement paste by wet grinded cement: Towards low carbon cementitious materials

Effect of organic alkali on hydration of GGBS-FA blended cementitious material activated by sodium carbonate

Properties and microstructure of a low-carbon clinker-free cementitious binder and its extrusion-based printing performance

Feasibility of Preparing Steel Slag–Ground Granulated Blast Furnace Slag Cementitious Materials: Synergistic Hydration, Fresh, and Hardened Properties

Modification mechanism of flue gas desulfurization gypsum on fly ash and ground granulated blast-furnace slag alkali-activated materials: Promoting green cementitious material

Properties of CO 2 -cured cement incorporating fly ash and slag subjected to further water curing

Study on the Properties and Hydration Mechanism of Calcium Carbide Residue-Based Low-Carbon Cementitious Materials

Circulating Fluidized Bed Fly Ash Mixed Functional Cementitious Materials: Shrinkage Compensation of f-CaO, Autoclaved Hydration Characteristics and Environmental Performance