Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Cyclic Deformation Behavior and Damage Mechanism of 316H Stainless Steel under Low-Cycle Fatigue Loading at 650 °C

The low-cycle fatigue, deformation and final fracture behaviour of an austenitic stainless steel

Multi-scale Deformation Behavior Investigation of 18cr–8ni Austenitic Steel Subjected to Low-Cycle Fatigue Loading

Effects of low-cycle fatigue on static mechanical properties, microstructures and fracture behavior of 304 stainless steel

Variation In Mechanical Properties, Microstructures And Fracture Behavior Of 304 Stainless Steel During Low-Cycle Fatigue

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Cyclic deformation mechanism and fracture behaviour of 316L stainless steel under thermomechanical fatigue loading

Investigation of Cyclic Deformation Behavior in the Surface Layer of 18cr–8ni Austenitic Stainless Steel Based on Vickers Microhardness Measurement

Depth-Sensing Indentation-Based Studies of Surface Mechanical Behavior and Fatigue Damage Evolution of an Austenitic Stainless Steel Subjected to Cyclic Straining

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Cyclic Deformation and Low-Cycle Fatigue for 316LN Stainless Steel under Non-proportional Loading

Cyclic behavior and damage mechanism of 304 austenitic stainless steel under different control modes

The strain ratio-dependent multiaxial low cycle fatigue behaviour and life prediction of 316L stainless steel based on critical plane at elevated temperature

Multiaxial low cycle fatigue behavior and life prediction method of 316LN stainless steel at 550 °C

Low Cycle Fatigue Behavior of Original Ferritic P92 Steel at High Temperature: Experiments and Simulations

Characterization of Low Cycle Fatigue Performance of New Ferritic P92 Steel at High Temperature: Effect of Strain Amplitude

Bending Fatigue Behavior of 316L Stainless Steel up to Very High Cycle Fatigue Regime

Investigation of low cycle fatigue crack propagation behavior of 316H steel at 550°C based on cyclic response and damage accumulation: experiment and modelling

Low cycle fatigue behavior of 316LN stainless steel: Effects of temperature, strain rate and strain amplitude