Contact Fatigue of Thin Hard Diamond-Like Carbon Films on M50 Steels under Cyclic Spherical Micro-Indentation

Kun Shu,Feihu Lin,Jianyun Wang,Zhen Li,Xinxin Ma,Chuanwei Zhang,Jiqiang Wu,Le Gu,Liqin Wang,Guanxiang Ge
DOI: https://doi.org/10.1016/j.triboint.2024.110019
IF: 5.62
2024-01-01
Tribology International
Abstract:Contact fatigue behaviors of thin hard diamond-like carbon (DLC) films on M50 steels during cyclic spherical micro-indentations were investigated. The stress-strain evolution of the entire system was analyzed by finite element methods. The film fracture mechanisms and interfacial bearing responses under monotonic and repeated contacts were comprehensively explored. Concentrated tensile and shear stresses were found to, respectively, govern the initiation and propagation of the surface ring cracks. Elevated tensile stresses at the initiation and epilogue of each indentation cycle enhanced bottom radial cracking. At the interfaces, the maximum tensile (6nmax) and shear (6tmax) stresses occurred at the end of unloading and loading processes, respectively. With increasing maximum indentation forces, 6nmax initially increased and then gradually decreased, while 6tmax increased monotonically.
What problem does this paper attempt to address?