Elevated-temperature and Post-Fire Performance of 6013-T6 High-Strength Aluminum Alloy: Experimental Study, Predictive Equations and Constitutive Models

Huyang Li,Ruoqiang Feng,Changjun Zhong

DOI: https://doi.org/10.1016/j.conbuildmat.2024.137442

IF: 7.4

2024-01-01

Construction and Building Materials

Abstract:High-strength aluminum alloy (HSAA) has received considerable attention in recent years due to its exceptional structural performance, cost-effectiveness, and environmental sustainability. However, its mechanical properties are notably affected by elevated temperatures. This study conducted 57 standard tensile tests to analyze the mechanical behavior of 6013-T6 HSAA at different temperatures and residual mechanical behavior under varied cooling techniques (cooling in air/water), encompassing Young's modulus, yield strength, ultimate strength, ultimate strain, and microstructure. The findings revealed that at temperatures above 200 degrees C, Young's modulus, yield strength, and ultimate strength of the material decreased significantly. At 400 degrees C, the yield strength and ultimate strength dropped to less than 10% of the values at ambient temperature, but could recover to around 50 % after cooling down. Furthermore, at temperatures below 200 degrees C, the mechanical properties after cooling remained similar to those at ambient temperature. However, beyond this threshold, the yield strength and ultimate strength after cooling exhibited a declining trend. A series of predictive equations were developed to predict the elevated-temperature retention factors and post-fire residual factors of these mechanical properties. Additionally, the accuracy of the design methods in current aluminum alloy specifications was evaluated, and a reliability analysis was conducted. It was found that the current aluminum alloy specifications provided inaccurate and scattered predictions for the elevated-temperature Young's modulus, while their predictions for other mechanical properties were accurate. The predictive equations proposed in this study were deemed reliable and secure. Finally, a two-stage Ramberg-Osgood constitutive model was introduced, which accurately predicts the stress-strain response of 6013-T6 HSAA under elevated-temperature and post-fire conditions.