Abstract:Titanium and titanium alloy materials are often made as medical implants. Surface properties of titanium medical implants play decisive roles for antibacterial and biological response and tissue biocompatibility. In this study, cathode arc evaporation (CAE) technology was used to deposit TiNb–Zr–Ta and nitrogen-doped TiNb–Zr–Ta coatings with nanostructures on the Ti–6Al–4V dental abutment screws. The deposited coatings were then oxidized at high temperature to produce different oxides on the surface of the coatings. The mechanical properties , antibacterial properties and biocompatibilities of the coatings were analyzed. The effect of coatings on the abutment screw loosening and removal torque between the abutment screw and the pure titanium implant fixture was studied by removal torque measurement. In addition, Staphylococcus aureus (S. aureus) was used for evaluating the antibacterial properties of coatings, and mouse fibroblasts (L929) were used for ISO 10993-5 cytotoxicity analyses to determine whether it had good biocompatibility. Nanolayered structures and multiphases of polycrystalline TiNb–Zr–Ta were obtained by co-deposition of Ta , Zr and TiNb. When small content of N was introduced, the TiNb–Zr–Ta(N) showed a polycrystalline TiNb–Zr–Ta where N atoms entered the metallic lattice at interstitial sites. After oxidation, oxide phases of Ta 2 O 5 , TiO 2 , Nb 2 O 5 and ZrO 2 were formed on the surface of TiNb–Zr–Ta and TiNb–Zr–Ta(N). Ta 2 O 5 was obtained on the surface of the coating prior to other oxides such as TiO 2 , Nb 2 O 5 and ZrO 2 . The deposited TiNb–Zr–Ta and TiNb–Zr–Ta(N) coatings had high contact angle and exhibited a hydrophobic feature, while the annealed TiNb–Zr–Ta–O and TiNb–Zr–Ta(N)–O showed hydrophilicity. The deposited TiNb–Zr–Ta had similar hardness and Young's modulus values to that of the uncoated Ti–6Al–4V. When N was doped, the TiNb–Zr–Ta(N) had the highest hardness and Young's modulus. The hardness of the annealed TiNb–Zr–Ta(N) coating only decreased slightly due to the small oxide layer of ∼140 nm. Compared with the uncoated Ti–6Al–4V, TiNb–Zr–Ta serial coatings deposited on abutment screws had higher removal torques, which prevented the abutment screw of dental implant from loosening after long-term use. The biocompatibility of TiNb–Zr–Ta serial coatings was similar to that of the uncoated Ti–6Al–4V. In addition, the oxidized TiNb–Zr–Ta and TiNb–Zr–Ta(N) coatings had excellent antibacterial properties. It is speculated that the resulting Ta 2 O 5 of both coatings may inhibit bacterial growth and improve the antibacterial effect. Based on the above advantages, the TiNb–Zr–Ta serial coatings are expected to have the potential to be applied to biomedical implants.

Enhanced Wear Resistance, Antibacterial Performance, and Biocompatibility Using Nanotubes Containing Nano-Ag and Bioceramics in Vitro

Fabrication and Biological Evaluation of the Coating Co‐doped Strontium and Zinc Nanoparticles on Porous Pure Titanium Surface by Hydrothermal Method

Zinc- and Strontium- Co-Incorporated Nanorods on Titanium Surfaces with Favorable Material Property, Osteogenesis, and Enhanced Antibacterial Activity.

In vitro and in vivo evaluation of antibacterial activity of polyhexamethylene guanidine (PHMG)-loaded TiO2 nanotubes.

Greater osteoblast and mesenchymal stem cell adhesion and proliferation on titanium with hydrothermally treated nanocrystalline hydroxyapatite/magnetically treated carbon nanotubes

Cytocompatibility and osteogenic activity of Ta-Ti-O nanotubes anodically grown on Ti6Al4V alloy

A novel biomedical TiN-embedded TiO 2 nanotubes composite coating with remarkable mechanical properties, corrosion, tribocorrosion resistance, and antibacterial activity

Electrochemical deposition multi-walled carbon nanotube coatings on the surface of Ti6Al4V alloy for enhancing its biotribological properties

The effects of feedback on referential communication of preschool children.

Mechanical, antibacterial and cytotoxic characteristics of nanolayered TiNb–Zr–Ta and nitrogen-doped TiNb–Zr–Ta coatings

Ag nanoparticles incorporated tannic acid/nanoapatite composite coating on Ti implant surfaces for enhancement of antibacterial and antioxidant properties

Fabrication and evaluation of silver modified micro/nano structured titanium implant

Strontium-Loaded Nanotubes of Ti-24Nb-4Zr-8Sn Alloys for Biomedical Implantation

A promising of alloying modified beta-type Titanium-Niobium implant for biomedical applications: Microstructural characteristics, in vitro biocompatibility and antibacterial performance

Fabrication of a Ag2O/SiO2/Ta2O5 nanocomposite coating for orthopaedic applications: Anticorrosion, photocatalytical and antimicrobial activities

Simultaneous improvement in mechanical properties, corrosion resistance and antibacterial properties of Ti-Ag sintered alloy with gradient nanostructure

Incorporation of Sr2+ and Ag nanoparticles into TiO2 nanotubes to synergistically enhance osteogenic and antibacterial activities for bone repair

Biocompatible Nanotube‐Strontium/polydopamine‐arginine–glycine–aspartic Acid Coating on Ti6Al4V Enhances Osteogenic Properties for Biomedical Applications

Report of the Advisory Panel on Alzheimer's Disease.

Enhanced Osseointegration and Antibacterial Action of Zinc-Loaded Titania-Nanotube-coated Titanium Substrates:In Vitroandin Vivostudies

Construction of Poly(Lactic-Co-Glycolic Acid)/Zno Nanorods/Ag Nanoparticles Hybrid Coating on Ti Implants for Enhanced Antibacterial Activity and Biocompatibility