Abstract:Three types of inorganic fillers - fumed nonporous nano-silica, synthesized mesoporous MCM-41 and microporous zeolite 4A, were incorporated into the PVDF matrix to prepare mixed matrix membranes. The objective of this study was to investigate the effects of pore structure and particle size of the inorganic fillers on the gas transport properties of the mixed matrix membranes. The membranes were characterized using thermogravimetric analysis (TGA), differential scanning calorimetry (DSC). X-ray diffraction (XRD), contact angle tests and scanning electron microscopy (SEM). The mechanical properties of the membranes were determined using a tensile stress-strain machine. With the incorporation of the inorganic fillers, the thermal stability of the composite membranes was reduced with lower degradation temperature while the melting temperature and crystallizing temperature seemed to be unaffected. The DSC results showed that the crystallinity of the composite membranes had increased when compared with the pure PVDF membrane. In addition, the incorporation of MCM-41 had induced PVDF crystalline phase transformation from alpha to beta phase. This phenomenon was not observed in PVDF/SiO2 and PVDF/4A composite membranes as indicated by the XRD results. In order to fully study the interface properties between the inorganic fillers and polymer chains, the density values of the membranes were experimentally determined and compared with the theoretical values. The experimentally determined density values of the composite membranes were lower than the theoretical values and the void volume fractions were calculated accordingly. The single gas (He, CO2, O-2 and N-2) permeabilities of the resulting membranes were carried out. The gas permeabilities of the three composite membranes exhibited similar behaviors, especially at lower inorganic filler loadings, although the inorganic fillers had different pore structures and particle sizes. The highest permeabilities for CO2 and O-2 were obtained by PVDF/4A 32% composite membrane, which were 3.26 and 0.41 Barrer, respectively, and the highest permeabilities for He and N2 were obtained by PVDF/MCM-41 32% composite membrane, which were 10.2 and 0.14 Barrer, respectively. These permeabilities are much higher than those of pure PVDF membrane. The highest selectivities of 120.7, 33.1 and 4.6 for He/N-2, CO2/N-2, and O-2/N-2, were obtained by the PVDF/SiO2 4%, PVDF/SiO2 32% and PVDF/SiO2 24%, respectively, which are also higher than those of pure PVDF membrane. (C) 2012 Elsevier B.V. All rights reserved.

Mixed Matrix Membranes Based on Nanoparticle, Nanorod, and Nanosheet MFI-Type Zeolites for Gas Separation

Mixed Matrix Membranes for C2H4/C2H6 Separation Using a Phosphate Anion-Pillared Microporous Material

Mixed Matrix Membranes Based on MFI Zeolite Nanosheets with Tunable Thickness for CO2/CH4 and H2/CH4 Separation

Enhanced Ethylene Transport of Mixed-Matrix Membranes by Incorporating Anion-Pillared Hybrid Ultramicroporous Materials Via in Situ Growth

Mixed Matrix Membranes Incorporating Amino-Functionalized ZIF-8-NH2 in a Carboxylic Polyimide for Molecularly Selective Gas Separation

MOF Nanosheet-Based Mixed Matrix Membranes with Metal-Organic Coordination Interfacial Interaction for Gas Separation.

Modified Zeolite/Polysulfone Mixed Matrix Membrane for Enhanced CO2/CH4 Separation

Carbon Nanotube-Based Mixed-Matrix Membranes with Supramolecularly Engineered Interface for Enhanced Gas Separation Performance

ZIF-301 MOF/6FDA-DAM polyimide mixed-matrix membranes for CO2/CH4 separation

Mixed matrix membranes for CO2 separations by incorporating microporous polymer framework fillers with amine-rich nanochannels

Mixed Matrix Membranes Containing UiO-66(Hf)-(OH)2 Metal–Organic Framework Nanoparticles for Efficient H2/CO2 Separation

Study of mixed matrix membranes with in situ synthesized zeolite imidazolate frameworks (ZIF-8, ZIF-67) in polyethersulfone polymer for CO2/CH4 separation

ZIF-8 Gel/PIM-1 Mixed Matrix Membranes for Enhanced H2/CH4 Separations

Pebax/two-dimensional MFI nanosheets mixed-matrix membranes for enhanced CO2 separation

Mixed Matrix Membranes (mmms) with Amine-Functionalized ZIF-L for Enhanced CO2 Separation Performance

Phenolic resin regulated interface of ZIF-8 based mixed matrix membrane for enhanced gas separation

Vesicles-Shaped Mof-Based Mixed Matrix Membranes With Intensified Interfacial Affinity And Co2 Transport Freeway

Preparation and Characterization of Mixed Matrix Membranes Based on Poly(vinylidene Fluoride) and Zeolite 4A for Gas Separation

ZIF-8 Hollow Nanotubes Based Mixed Matrix Membranes with High-Speed Gas Transmission Channel to Promote CO2/N2 Separation

High Performance Gas Separation Mixed Matrix Membrane Fabricated by Incorporation of Functionalized Submicrometer-Sized Metal-Organic Framework

Preparation and Characterization of Mixed Matrix Membranes Based on PVDF and Three Inorganic Fillers (fumed Nonporous Silica, Zeolite 4A and Mesoporous MCM-41) for Gas Separation