White-Light Emission From A Single-Emitting-Component Ca9gd(Po4)(7):Eu2+,Mn2+ Phosphor With Tunable Luminescent Properties For Near-Uv Light-Emitting Diodes
Ning Guo,Hongpeng You,Yanhua Song,Mei Yang,Kai Liu,Yuhua Zheng,Yeju Huang,Hongjie Zhang
DOI: https://doi.org/10.1039/c0jm01860k
2010-01-01
Journal of Materials Chemistry
Abstract:Ca9Gd(PO4)(7) and Ca9Gd(PO4)(7):xEu(2+), yMn(2+) were synthesized by solid-state reaction. The refinement confirmed that Ca9Gd(PO4)(7) belongs to space group R3c (No. 161) with unit cell parameters a = 10.4526 angstrom, c 37.3769 angstrom, V 3536.61 angstrom(3), and Z = 6. Upon the excitation from 250 to 430 nm, the Ca9Gd(PO4)(7):xEu(2+), yMn(2+) phosphors exhibit a broad blue-green emission band at 490 nm and a red emission band at 645 nm, which originate from the Eu2+ and Mn2+ ions, respectively. The varied emitted color from blue-green through white and eventually to red can be achieved by properly tuning the relative ratio of the Eu2+ to Mn2+ ions in the phosphors through the energy transfer from the Eu2+ and Mn2+ ions. The energy transfer from Eu2+ to Mn2+ was demonstrated to be a resonant type via a dipole-quadrupole reaction by the luminescence spectra, energy transfer efficiency, and decay curves of the phosphors. Furthermore, the critical distance of the Eu2+ and Mn2+ ions has also been calculated. More importantly, compared to the multiple emitting components of white LEDs system, single-emitting-component phosphors would enable easy fabrication with perfect stability and color reproducibility.