Abstract:The surface reconstruction process happened to electrocatalysts for creating active sites, which has been evidenced to determine the electrocatalytic activity for water splitting. Herein, the electrolyte conditions (i.e., OH- and Fe3+) were engineered to manipulate the surface reconstruction process happened to nickel foam (NF) for forming Fe-incorporated gamma-NiOOH phases, and a low overpotential of only 267 mV could be achieved for alkaline oxygen evolution reaction (OER) at the current density of 100 mA cm(-2). More excitingly, the anion exchange membrane water electrolyzer (AEMWE) with Fe-incorporated gamma-NiOOH phases created on NF as the anode could survive from a 100-h operation at an industrial-level current density of 1 A cm(-2). The OH- ions in the electrolyte could promote the dissolution-redeposition process with created gamma-NiOOH phases active for the OER, and meanwhile boost the incorporation of Fe into the formed gamma-NiOOH phases, thermodynamically facilitating the formation of O* intermediates for improved OER performance.

Manipulating the Electrochemical Surface Reconstruction of Nickel Foam Via Electrolyte Engineering for Efficient Oxygen Evolution Reaction at Industrial-Level Current Density