One-step and Universal Fabrication of MXene/metal Sodiophilic Frameworks Via Lewis Acidic Etching Toward Dendrite-Free Sodium Metal Anodes

Pengfei Huang,Hangjun Ying,Zhao Zhang,Zuojie Xu,Shunlong Zhang,Wei-Qiang Han

DOI: https://doi.org/10.1016/j.cej.2024.153490

IF: 15.1

2024-01-01

Chemical Engineering Journal

Abstract:Although MXene-based 3D scaffolds have boosted the cyclability of Na metal, the complex and harsh synthetic process deteriorates their practical application. Herein, a series of MXene/metal sodiophilic frameworks are constructed through one-step Lewis acidic etching, and metal nanoparticles are uniformly distributed on the surface or intercalated into the large interlayer gaps of MXenes. Notably, MXenes with superior Na+/electron transport kinetics and mechanical flexibility remarkably reduce the local current density, homogenize Na+ flux and cushion huge volume change of Na metal. Moreover, sodiophilic species including MXenes and metals effectively induce Na uniform nucleation and smooth deposition among the 3D matrixes, leading to dendrite-free morphology. Consequently, MXene/metal hosts exhibit stable Na plating/stripping process for 900 cycles with high average Coulombic efficiencies of 99.9% (2 mA cm-2, 1 mAh cm-2). The MXene/metal-Na symmetric cells achieve low overpotentials of less than 15 mV and stable cycling for 2200 h (2 mA cm-2, 4 mAh cm-2). When paired with Na3V2(PO4)3 cathode, the full cells with a low N/P ratio (around 2) demonstrate high discharge capacity and excellent long-term cyclic performance over 600 cycles. The presented universal, safe and one-step approach in fabricating MXene/metal scaffolds shows bright prospects and may promote the development of alkali metal-based batteries.