Abstract:Compared to rare-earth doped glasses, bismuth-doped glasses hold promise for super-broadband near-infrared (NIR) photoemission and potential applications in optical amplification. However, optically active bismuth centers are extremely sensitive to the properties of the surrounding matrix, and also to processing conditions. This is strongly complicating the exploitation of this class of materials, because functional devices require a very delicate adjustment of the redox state of the bismuth species, and its distribution throughout the bulk of the material. It also largely limits some of the conventional processing routes for glass fiber, which start from gas phase deposition and may require very high processing temperature. Here, we investigate the influence of melting time and alkali addition on bismuth-related NIR photoluminescence from melt-derived germanate glasses. We show that the effect of melting time on bismuth-related absorption and NIR photoemission is primarily through bismuth volatilization. Adding alkali oxides as fluxing agents, the melt viscosity can be lowered to reduce either the glass melting temperature, or the melting time, or both. At the same time, however, alkali addition also leads to increasing mean-field basicity, what may reduce the intensity of bismuth-related NIR emission. Preferentially using Li2O over Na2O or K2O presents the best trade-off between those above factors, because its local effect may be adverse to the generally assumed trend of the negative influence of more basic matrix composition. This observation provides an important guideline for the design of melt-derived Bi-doped glasses with efficient NIR photoemission and high optical homogeneity.

Bismuth blended germanium base optical glass

Bismuth- and Aluminum-Codoped Germanium Oxide Glasses for Super-Broadband Optical Amplification

Investigations on Bismuth and Aluminum Co-Doped Germanium Oxide Glasses for Ultra-Broadband Optical Amplification

Inhomogeneous broadening, luminescence origin and optical amplification in bismuth-doped glass.

Infrared Luminescence and Amplification Properties of Bi-doped GeO 2 − Ga 2 O 3 − Al 2 O 3 Glasses

Novel Bi-Doped Glasses for Broadband Optical Amplification

Broadband Optical Amplification in Bi-Doped Germanium Silicate Glass

Homogeneity of Bismuth-Distribution in Bismuth-Doped Alkali Germanate Laser Glasses Towards Superbroad Fiber Amplifiers.

Effect of Ga2O3 on the spectroscopic properties of erbium-doped boro-bismuth glasses

1.53 μm luminescent properties and energy transfer processes of Er3+/Yb3+ co-doped bismuth germanate glass laser material

Near Infrared Broadband Emission of Bismuth-Doped Aluminophosphate Glass

Broadband tunable near-infrared emission of Bi-doped composite germanosilicate glasses

Optical properties of bismuth-doped SiO2- or GeO2-based glass core optical fibers

Effect of SiO 2 on optical properties of bismuth-doped B 2 O 3 –GeO 2 –SiO 2 glasses

Superbroadband 1310 nm emission from bismuth and tantalum codoped germanium oxide glasses.

Mixed Network Effect of Broadband Near‐Infrared Emission in Bi‐Doped B2O3‐GeO2 Glasses

Effect of SiO2 on Optical Properties of Bismuth-Doped B2O3–GeO2–SiO2 Glasses

Bismuth-doped glass microsphere lasers

Intense 2.7 µm emission and structural origin in Er3+-doped bismuthate (Bi2O3-GeO2-Ga2O3-Na2O) glass

Infrared Broadband Emission of Bismuth-Doped Barium-Aluminum-borate Glasses.

Bismuth-doped zinc aluminosilicate glasses and glass-ceramics with ultra-broadband infrared luminescence