Mn-Cr mixed oxide adsorbents with high SO2 resistance for elemental mercury removal from coal-fired flue gas
Senyuan Wang,Dong Ye,Xin Liu,Haining Wang,Wei Ma,Hui Liu
DOI: https://doi.org/10.1016/j.jiec.2023.03.041
IF: 6.76
2023-05-03
Journal of Industrial and Engineering Chemistry
Abstract:A series of Mn-Cr mixed oxide adsorbents were obtained using co-precipitation method. Then, an investigation was conducted into the effects of Mn/Cr molar ratio, reaction temperature, calcination temperature, initial mercury concentration and flue gas constituents on the outcome of elemental mercury removal. Specifically, the MnCr1:3 with an optimal Mn/Cr molar ratio performed best in the efficiency of mercury removal (>95.4%) in a wide temperature range (100–250 °C). The physicochemical properties and the mechanism were characterized by N 2 adsorption–desorption, SEM, XRD, NH 3 -TPD, H 2 -TPR, XPS and Hg-TPD in combination. According to the research results, mercury removal was facilitated by MnCr1:3 due to its larger surface area, smaller crystallite sizes, higher acidity and redox properties. Sulfur dioxide promoted elemental mercury capture for MnCr1:3 when different concentrations of SO 2 existed in the flue gas. The relative activity over MnCr1:3 approached 100% after five regeneration cycles. Due to the combined effect of manganese and chromium, there was an increase in the concentration of high valence metal elements and surface adsorbed oxygen. MnCr1:3 had the highest content of Cr 6+ and adsorbed oxygen species, for which they played a vital role in the outcome of mercury removal. Graphical abstract Download : Download high-res image (213KB) Download : Download full-size image Effectively weakening the bond strength of Zn-S in S-Zn-S on ZnS is of great significance to the improvement of its performance for the urgent disposal of liquid Hg 0 leakage indoors. In this work, ZnS was loaded on three common supports (i.e., TiO 2 , SiO 2 , and Al 2 O 3 ) to further improve its performance for capturing high concentrations of Hg 0 indoors. After being loaded on TiO 2 , the S-Zn-O bond was present on ZnS, and the bond strength of Zn-S in S-Zn-O was significantly weaker than that in S-Zn-S because Zn 2+ preferred to O 2− than S 2− . Hence, physically adsorbed Hg 0 was much easier to bond with S in S-Zn-O than that in S-Zn-S to form HgS. Therefore, TiO 2 showed a novel support effect on ZnS for Hg 0 capture, and the Hg 0 capture performance of ZnS/TiO 2 was greatly better than those of ZnS, ZnS/SiO 2 , and ZnS/Al 2 O 3 . Moreover, the promotion mechanism of ZnO loading on Hg 0 adsorption onto TiO 2 -S was discovered after comparing the Hg 0 adsorption kinetic parameters of TiO 2 -S and ZnS/TiO 2 . The promotion of ZnO loading was primarily related to the notable increase in the content of S 2− that can bond with physically adsorbed Hg 0 , which predominantly resulted from the strong interaction of ZnO/TiO 2 with H 2 S. This study explored the photothermal catalytic oxidation of Hg 0 by using S-scheme heterojunction CeO 2 /TiO 2 modified by reduced graphene oxide (rGO) at 100-200 °C. The surface properties of self-prepared photothermal catalysts were characterized by BET, SEM, TEM, EDS, XRD, Raman, UV–Vis, XPS, EPR, and UPS. The crystal structure of TiO 2 was mainly anatase and the nano-sized CeO 2 /TiO 2 was uniformly distributed on the surface of the rGO sheet. The oxidation efficiency of Hg 0 decreased with reaction temperature in the order of Ƞ 100 °C = Ƞ 150 °C > Ƞ 200 °C , implying that the oxidation of Hg 0 was controlled by mass transfer governed by adsorption instead of photothermal catalytic reaction. Both photo- and thermos-catalytic reaction mechanisms were involved in the oxidation of Hg 0 at 100–200 °C. Moreover, rGO-modified CeO 2 /TiO 2 could tolerate multi-pollutants (SO 2 and NO) except for 100 ppm NO, which slightly reduced the oxidation efficiency of Hg 0 . The rationally engineered integration of structural and electronic properties allows to obtain a desirable remediator for permanent Hg 0 sequestration. Herein, one novel two-dimensional hierarchical FeSe 2 /g-C 3 N 4 nano-heterojunction was purposefully synthesized via a modified initial wetting impregnation followed by hydrothermal selenization method and further demonstrated to be an efficient trap for Hg 0 immobilization -Abstract Truncated-
engineering, chemical,chemistry, multidisciplinary