Hybrid Pseudocapacitance/co-Intercalation Mechanisms of TiO2/graphite Anodes for Rapid Sodium-Ion Storage

Ze-Rui Yan,Da-Fu Tang,Bin-Hao Wang,Xiao-Juan Huang,Xia Zou,Si-Cheng Fan,Yan Wu,Tong Shu,Qiu-Long Wei
DOI: https://doi.org/10.1007/s12598-024-02848-w
IF: 6.318
2024-01-01
Rare Metals
Abstract:Developing anode materials with high specific/volumetric capacities, high-rate capability, long-term cycles and low cost is significant for advanced sodium-ion storage. Herein, we report the hybrid TiO2/graphite (TiO2/G) anodes for fast (dis)charging sodium-ion storage. Taking advantage of the rapid pseudocapacitive surface-redox on anatase TiO2 nanoparticles (NPs) and fast [Na(diglyme)(x)](+) co-intercalation into graphite, the hybrid anodes display excellent rate capabilities. Additionally, the TiO2 NPs are able to fill into the interspaces among graphite flakes and the graphite provides continuous electron pathways, which largely boosts the volumetric capacities and rate performance. Benefitting from the synergistic effects, the hybrid electrodes display excellent comprehensive electrochemical performance. At the thick-film electrodes (a single-side mass loading of 10 mgcm(-2)), the hybrid TiO2/G anode, in a ratio of 40/60 by weight, exhibits high gravimetric and volumetric capacities (71 mAhg(-1)/152 mAhcm(-3)) at a high current density of 20 mAcm(-2) (2 Ag(-1)), which are higher than those of the graphite (61 mAhg(-1)/121 mAhcm(-3)), TiO2 NPs (37 mAhg(-1)/72 mAhcm(-3)) and hard carbon (19 mAhg(-1)/23 mAhcm(-3)) anodes. The TiO2/G hybrid anodes with excellent comprehensive electrochemical performance display promising potential for high-power sodium-ion batteries and capacitors.
What problem does this paper attempt to address?